Mn-enhanced Li-Ni-Mn-Zn nano-ferrites: Synthesis, characterization, and evaluations of structural, morphological, magnetic, and dielectric features
Moiful Alam,Mosarof Hossain Sarkar,Asif Parvez,Kamrul Alam Khan
DOI: https://doi.org/10.1016/j.jmmm.2024.171783
IF: 3.097
2024-01-29
Journal of Magnetism and Magnetic Materials
Abstract:Applying an established technique known as sol–gel autocombustion, Mn-enhanced Li-Ni-Mn-Zn (LNMZ) ferrite nanoparticles with nominal compositions of Li 0.15 Ni 0.20 Mn 0.10+x Zn 0.40-x Fe 2.15 O 4 , where x = 0.00 to 0.10 in the step of 0.05, were synthesized in this investigation. Prepared disk- and toroid-shaped specimens were sintered in the air for 5 h at different temperatures. The XRD was utilized to examine structure-related indicators like phase identification, crystallite size, and the lattice constant of the samples. The crystallite size of the specimens was in the range of 41 to 46 nm, which was calculated at the sintering temperature (T S ) of 1523 K. Theoretical and bulk densities declined with enhanced Mn concentration, whereas the lattice constant and porosity improved slightly. As expected, density rises and porosity decreases with increasing T S (from 1373 to 1523 K). The average grain diameter was found to increase with increasing Mn 2+ ions, which was determined by the linear intercept technique. For the maximum Mn 2+ ions (x = 0.10) of this investigation at T S = 1523 K, the real part of initial permeability achieves its largest value (=439), and improves 27 % in comparison with the preliminary composition (x = 0.00). For the same sample, the relative quality factor, significantly enhanced, reaches the highest value (=20015), which is 60 % larger compared to the parent composition of the LNMZ ferrites. With the addition of the Mn content, the Néel temperature declines from 573 to 558 K. The real part of the dielectric constant, dielectric loss tangent, the real part of the impedance, the Cole-Cole plots, and ac conductivity were analyzed to disclose the facts about the dielectric features of the current LNMZ nano-ferrite materials.
materials science, multidisciplinary,physics, condensed matter