Abstract:Mn1−xZnxFe2O4 (x = 0.2–0.8) ferrite samples were successfully prepared by the sol–gel method. X-ray diffraction study reveals that single cubic spinel phase was formed in Mn1−xZnxFe2O4 samples. The SEM micrographs revealed that the microstructures change significantly with different Zn2+ doping concentration and sintering temperature while the grain size grow up to 9.48 μm for Mn0.6Zn0.4Fe2O4 sample sintered at 1100 °C. Further, the dielectric and magnetic measurements indicated that both Zn2+ doping and sintering temperature could affect both electrical and magnetic parameters such as dielectric constant and saturation magnetization in a great manner. The Mn0.6Zn0.4Fe2O4 sample sintered at 1100 °C for 8 h is found to show the largest M s value (77.30 emu/g) in this work. These results indicate that Zn2+ doping or sintering temperature can adjust the microstructures, dielectric and magnetic properties of Mn1−xZnxFe2O4 ferrites.

Effect of Zn2+ Doping on the Structural, Magnetic and Dielectric Properties of MnFe2O4 Prepared by the Sol–gel Method