Enhanced adsorption performance of PPy/TiO 2 prepared on surface of TiO 2 without calcination

Jingjing Li,Jiangtao Feng,Wei Yan

DOI: https://doi.org/10.1007/s42452-019-0628-8

2019-01-01

SN Applied Sciences

Abstract:The PPy/TiO 2 composites were synthesized by polymerizing pyrrole monomer on the surface of TiO 2 calcined at different temperatures. The results of Fourier Transform Infrared spectroscopy, X-ray diffraction, Temperature programmed desorption, X-ray photoelectron spectroscopy and Zeta potential showed that the type and amount of the active groups on TiO 2 surface decreased with the increase of calcination temperature, leading to a significant decline in its adsorption capacity for Acid Red G (ARG) and Methylene Blue (MB). This also had a significant influence on the physicochemical property and adsorption performance of PPy/TiO 2 . The prepared PPy/TiO 2 composite exhibited an enhanced adsorption capacity for ARG and MB. The adsorption ability of PPy/TiO 2 was the strongest when TiO 2 was not calcined and gradually decreased with the increase of the calcination temperature of TiO 2 . The PPy/TiO 2 composite without calcination was chosen to investigate its adsorption performance. The results showed that the adsorption behaviors of ARG and MB on PPy/TiO 2 were described by the pseudo-second-order and Langmuir isotherm models with the maximum adsorption amount of 424.75 and 439.61 mg/g for ARG and MB, respectively. Finally, the surface chemical properties of TiO 2 seriously affected the adsorption performance of PPy/TiO 2 . The PPy/TiO 2 composite could possess excellent adsorption performance when the selected TiO 2 contained more hydroxyl and carboxyl groups. Graphical abstract