Abstract:Nanowires have a wide range of applications, such as transparent electrodes, Li-ion battery anodes, light-emitting diodes, solar cells, and electronic devices. Currently, aluminum (Al) nanowires can be synthesized by thermally induced substitution of germanium (Ge) nanowires, chemical vapor deposition on other metal substrates, and template-assisted growth methods. However, there are still challenges in fabricating extremely high-purity nanowires, large-scale manufacturing, and simplifying the synthesis process and conditions. Here, we report for the first time that single-crystal Al nanowires can be one-step, in situ synthesized on a reduced graphene oxide (RGO) substrate on a large scale without using any catalysts. Through a simple high temperature treatment process, commercial micro-sized Al powders in RGO film were transformed into a single-crystal Al nanowire with an average length of 1.2 μm and an average diameter of 18 nm. The possible formation mechanism of the single-crystal Al nanowires is proposed as follows: hot aluminum atoms eject from the pristine aluminum/alumina core/shell structure of Al powders when they build up enough energy from the thermal stress under high temperature and confined space conditions, which is supported by both experimental and computational results. The method introduced here can be extended to allow the synthesis of one-dimensional highly reactive materials, like alkali metal nanowires, in confined spaces.

Synthesis of Crystalline Alumina Nanowires and Nanotrees

Ultrafast growth of single-crystalline Si nanowires

Synthesis and Characterization of Single-Crystalline Alumina Nanowires

One-Step, Catalyst-Free, Scalable in Situ Synthesis of Single-Crystal Aluminum Nanowires in Confined Graphene Space

Catalyst-free growth of single-crystalline alumina nanowire arrays

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

Interface catalytic reduction of alumina by nickle for the aluminum nanowire growth: Dynamics observed by in situ TEM

Fabrication of ZnO/Al2O3 core–shell nanostructures and crystalline Al2O3 nanotube

Hydrothermal Synthesis and Characterization of Uniform Α-Feooh Nanowires in High Yield

Synthesis of alumina nanotubes using carbon nanotubes as templates

Controlled Synthesis and Characterization of 10 Nm Thick Al2O3 Nanowires

In situ catalytic growth of Al2O3 and Si nanowires

Fabrication of Alumina Nanowires via Anodic Oxidation of Aluminum

Synthesis and Characterization of Gibbsite Nanostructures

Synthesis of Aluminum Nitride Nanowires from Carbon Nanotubes

Silicon nanowires fabricated by thermal evaporation of silicon monoxide

Catalysed Growth of Novel Aluminium Oxide Nanorods

Single Crystalline Cr2O3 Nanowires/nanobelts: CrCl3 Assistant Synthesis and Novel Magnetic Properties

Synthesis of Silicon Carbide Nanowires in a Catalyst-Assisted Process

Carbon-Assisted Synthesis of Aligned Zno Nanowires

Controlled Growth of Large-Area, Uniform, Vertically Aligned Arrays of α-Fe<sub>2</sub>O<sub>3</sub>Nanobelts and Nanowires