Ca {sub 3}(PO {sub 4}){sub 2} coating of spherical Ni (OH){sub 2} cathode materials for Ni MH batteries at elevated temperature

Xiangming He,Jianguo Ren,Wen Li,Changyin Jiang,Chunrong Wan

2006-01-01

Abstract:Calcium phosphate was used for surface modification of spherical nickel hydroxide to improve its high temperature performance at the first time due to its low cost. The Ca {sub 3}(PO {sub 4}){sub 2} and Co (OH){sub 2} coated nickel hydroxides were prepared by precipitation of Ca {sub 3}(PO {sub 4}){sub 2} on the surface of spherical nickel hydroxide, followed by precipitation of Co (OH){sub 2} on its surface. The optimum coating content of calcium was around 2%(atomic concentration) to obtain high discharge capacity both at 25 and 60 {sup o} C. It was shown that the discharge capacity of nickel hydroxide at higher temperatures was improved by coating of Ca {sub 3}(PO {sub 4}){sub 2} and cobalt hydroxide. The high temperature performances of the sealed AA-sized nickel-metal hydride (Ni-MH) batteries using Ca/Co coated nickel hydroxide as positive electrodes were carried out, showing much better than those using uncoated or only Co (OH){sub 2} coated nickel hydroxide electrodes. The charge acceptance of the battery using 2% Ca and 2% Co coated nickel hydroxide reached 81% at 60 {sup o} C, where the charge acceptances for uncoated and only Co (OH){sub 2} coated nickel hydroxide were only 42 and 48%, respectively. It has shown that the Ca/Co coating is an effective way to improve the