Abstract:The 2195 Al-Cu-Li alloy is widely utilized for the fabrication of key aerospace vehicle components; hence, an in-depth understanding of its hot deformation behavior is essential for consistently achieving high-performance products. In this study, isothermal compression tests were performed on 2195 Al-Cu-Li alloy ingots in the temperature and strain rate ranges of 250–500 °C and 10 −3 -1 s −1 , respectively. A processing map was established to predict the workability under different conditions. The corresponding microstructures were examined to reveal their hot deformation mechanism. Results demonstrated that the processing map was divided into four distinct domains. The unstable zone was located in the 250–375 °C/10 −1.5 -1 s −1 and 250–275 °C/10 −2.5 –10 −1.5 s −1 , temperature/strain rate regimes, in which deformation bands and flow localization were observed. The deformation bands blocked dislocations and compromised the dynamic recrystallization (DRX) behavior, hence damaging the microstructure. Further, large coarse T 1 phases precipitated in the 325–410 °C/10 −2.5 –10 −3 s −1 regime, which led to the formation of heterogeneities in the microstructure, corresponding to a minimum workability in the processing map. The optimal hot-working domain for the 2195 alloy was determined to be 460–500 °C/10 −3 –10 −2 s −1 , and the dominating hot deformation mechanisms were DRX and dynamic recovery (DRV). Specifically, continuous and discontinuous DRX behaviors dominated in the 300–400 °C/10 −3 s −1 and 450–500 °C/10 −3 s −1 regimes, respectively. DRX gradually weakened as the strain rate increased at 500 °C. Further, the weakening of DRX was only minimally affected by temperature at 400–500 °C during high-speed deformation (1 s −1 ). The results reported herein can provide valuable insights into the hot working of Al-Cu–Li alloys.

Constitutive Behavior and Hot Workability of Multi-Direction Forged T2 Copper During Hot Compression Deformation

Dislocation Density-Based Constitutive Model and Processing Map for T2 Copper During Isothermal and Time-Variant Deformation

Hot Deformation Constitutive Model and Processing Maps of Homogenized Al–5Mg–3Zn–1Cu Alloy

Hot Workability and Microstructure Evolution of Homogenized 2050 Al-Cu-Li Alloy during Hot Deformation

Hot Deformation Behavior and Microstructure Evolution of a Graphene/Copper Composite

Characterization of Hot Deformation Behavior and Processing Map of As-Cast H13 Hot Work Die Steel

Hot Deformation And Processing Window Optimization Of A 70mnsicrmo Carbide-Free Bainitic Steel

Microstructural and constitutive relationship in process modeling of hot working: The case of a 60Mg-30Pb-9.2Al-0.8B magnesium alloy

Characterization of Hot Deformation Behavior and Processing Maps of Homogenized Al-Mg-Si-Sc-Zr Alloys

The Deformation Behavior and Microstructure Evolution of a Mn- and Cr-Containing Al-Mg-Si-Cu Alloy During Hot Compression and Subsequent Heat Treatment

Study of Dynamic Recrystallization Behavior of T2 Copper in Hot Working Conditions by Experiments and Cellular Automaton Method

Hot Deformation Behavior and Microstructure Evolution of Al-7.92 Zn-1.64 Mg-2.00 Cu Alloy

Hot deformation behavior and microstructural evolution of the Al-Cu-Li alloy: A study with processing map

Hot Deformation Behavior of Homogenized Al-7.8Zn-1.65Mg-2.0Cu (wt.%) Alloy

Hot Deformation Behavior of Cu-2.7Be Alloy During Isothermal Compression

Microstructural Evolution and Hot Deformation Behavior of Cu‐Containing Twinning‐Induced Plasticity Steel

Hot Deformation Behavior and Processing Maps of an As-Cast Al-5Mg-3Zn-1Cu (wt%) Alloy

Constitutive equation and dynamic recovery mechanism of high strength cast Al-Cu-Mn alloy during hot deformation

Hot Deformation Behavior and Processing Maps of Znsno3/Cu Composites

Investigation of Constitutive Relationship and Dynamic Recrystallization Behavior of 22mnb5 During Hot Deformation

Hot Deformation Characteristics and Processing Parameter Optimization of Al–6.32Zn–2.10Mg Alloy Using Constitutive Equation and Processing Map