Ligand-Induced Chirality in Asymmetric CdSe/CdS Nanostructures: A Close Look at Chiral Tadpoles
Junjie Hao,Yiwen Li,Jun Miao,Rulin Liu,Jiagen Li,Haochen Liu,Qiushi Wang,Huan Liu,Marie-Hélène Delville,Tingchao He,Kai Wang,Xi Zhu,Jiaji Cheng,Marie-Hélène Delville
DOI: https://doi.org/10.1021/acsnano.0c03909
IF: 17.1
2020-08-03
ACS Nano
Abstract:Ligand-induced chirality in asymmetric CdSe/CdS core–shell nanocrystals (NCs) has been extensively applied in chiral biosensors, regioselective syntheses and assemblies, circularly polarized luminescence (CPL), and chiroptic-based devices due to their excellent physiochemical properties, such as the tunable quantum confinement effects, surface functionality, and chemical stability. Herein, we present CdSe/CdS NCs with various morphologies such as nanoflowers, tadpoles, and dot/rods (DRs) with chirality induced by surface chiral ligands. The observed circular dichroism (CD) and CPL activities are closely associated with the geometrical characteristics of the nanostructures, such as the shell thickness and the aspect ratio of the CdSe/CdS NCs. Furthermore, <i>in situ</i> observations of the growth of tadpoles with a single tail indicate that the CD response is mainly attributed to the CdS shell, which has a maximum tail length of ∼45 nm (approximately λ/10 of the incident light wavelength). On the other hand, the CPL activity is only related to the CdSe core, and the activity benefits from a thin CdS shell with a relatively high photoluminescence quantum yield (QY). Further theoretical models demonstrated the aspect-ratio-dependent <i>g</i>-factor and QY variations in these asymmetric nanostructures. These findings provide insights into not only the asymmetric synthesis of CdSe/CdS NCs, but also the rational design of CdSe/CdS nanostructures with tunable CD and CPL activities.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.0c03909?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.0c03909</a>.Additional data and figures describing the UV–vis absorptions and PL spectra of the different morphologies (Figures S1, S7, and S9), the relationship between PL spectra and shapes of different NCs (Figure S2), CD spectra and the corresponding anisotropic <i>g</i><sub>CD</sub>-factor variation with wavelength (Figures S3, S4, S6, and S8), and the <i>g</i><sub>lum</sub> value variation with the wavelength of the morphologies exhibiting CPL activity (Figures S5 and S10); theoretical calculations and modeling of the <i>g</i>-factor and QY (Figure S11 and S12); physical properties of NCs with different shapes in the organic phase (Table S1); diameter standard deviation ratio study of NCs with different shapes (Table S2); CD anisotropy <i>g</i>-factors and CPL <i>g</i><sub>lum</sub> for chiral cadmium-based NCs induced by small-molecule chiral ligands (Table S3); CD anisotropy factors of <span class="smallcaps smallerCapital">d</span>-Cys-CdSe/CdS NCs (Table S4); CPL anisotropy factors of <span class="smallcaps smallerCapital">l</span>-Cys-CdSe/CdS NCs in water (Table S5); CD anisotropy factors of <span class="smallcaps smallerCapital">d</span>-Cys-CdSe/CdS Tadpole-I for different reaction times (Table S6); physical properties of tadpoles at different reaction times in the organic phase (Table S7); physical properties of tadpoles with different lengths in organic phase (Table S8); CD anisotropy factors of <span class="smallcaps smallerCapital">d</span>-Cys-CdSe/CdS Tadpole-I with different lengths (Table S9); CPL anisotropy factors of <span class="smallcaps smallerCapital">l</span>-Cys-CdSe/CdS Tadpole-I with different lengths (Table S10) (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.0c03909/suppl_file/nn0c03909_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology