Abstract:<p class="Para">Nuclear graphite that can be used in molten salt reactors, one of the main types of fourth-generation nuclear reactors, has the properties of high purity, high density, and radiation resistance, and it also has a special pore structure that prevents infiltration of the molten salt fuel. The nuclear graphites IG-110, NBG-18, and NG-CT-50 were characterised using X-ray computed tomography (CT) to understand their internal pore structures. The porosities, isolated pore volumes, and connected pore volumes were obtained. The average diameter of connected pores in IG-110, NBG-18, and NG-CT-50 were 9.9, 10.4 and 9.5 μm, respectively, but the nuclear graphite NBG-18 had the broadest diameter range for connected pores, with many of > 25 μm. To further analyse the connected pores, pore throat networks were established based on the connected porosities. The pore throats, channel lengths, and coordination numbers of the connected pores were herein quantitatively analysed. Among IG-110, NBG-18, and NG-CT-50, the average diameters of the throats were 4.5, 5.2, and 4.6 μm, and the peak throat diameters were 1.8, 2.6, and 1.2 μm, respectively, but the NBG-18 pore throat distribution also included multiple peaks at larger diameters (16–20 μm), which was consistent with findings from the mercury intrusion test. Our statistics based on the pore throat networks suggested that NBG-18 is the most easily infiltrated by molten salt among the three nuclear graphite samples, while NG-CT-50 is the most difficult. The quantitative information from the pore throat modelling could be a basis for future studies on liquid flow simulations inside graphite.</p><h3 class="Heading">Graphic </h3> <a href="https://media.springernature.com/original/springer-static/image/art%3A10.1007%2Fs10921-020-0659-5/MediaObjects/10921_2020_659_Figa_HTML.jpg"><span class="u-screenreader-only">Open image in new window</span></a>

Porosity properties and molten salt impregnation characteristics of nuclear graphites

Irradiation Characteristics of Non-Impregnated Micropore Graphite for Use in Molten Salt Nuclear Reactors

Microstructure and Molten Salt Impregnation Characteristics of A Micro-Fine Grain Graphite for Use in Molten Salt Reactors

Pore Structure of Nuclear Graphite Obtained via Synchrotron Computed Tomography

Microstructural characterization of the CGB graphite grade from the molten salt reactor experiment

Effects of Impurities and Additives on Interactions of Nuclear-Grade Graphite with Molten LiF-NaF-KF

Irradiation resistance study of binderless nanopore-isotropic graphite for use in molten salt nuclear reactors

High temperature in-situ synchrotron-based XRD study on the crystal structure evolution of C/C composite impregnated by FLiNaK molten salt

Graphite-Molten Salt Considerations for Components in Nuclear Applications

Densification of A3-3 Matrix Graphite to Inhibit the Infiltration of Liquid FLiBe Salt in Molten Salt Reactors

Preliminary analysis of the irradiation deformation of a typical molten salt reactor graphite component

Densification of matrix graphite for spherical fuel elements used in molten salt reactor via addition of green pitch coke

Mesocarbon microbead densified matrix graphite A3-3 for fuel elements in molten salt reactors

Neutronic effect of graphite dimensional change in a small modular molten salt reactor

The Influence of Pores on Irradiation Property of Selected Nuclear Graphites

An Innovative Spherical Fuel Element to Inhibit the Infiltration of Liquid Fluoride Salt in Molten Salt Reactor

The Study of Continuous Core Zoning to Extend the Graphite Component Irradiation Lifespan in Molten Salt Reactor

Measurement of the Diffusion Coefficient of Xenon in Self-Sintered Nanopore Graphite for Molten Salt Reactor

Characterization of Porosity Development in Oxidized Nuclear Graphite

Effect of porosity on oxidation of nuclear grade graphite

Superior molten FLiBe salt barrier properties of a mesophase–pitch-based carbon/carbon composite prepared via hot isostatic pressing