Friction and wear properties of matrix graphite in spherical fuel element for HTR

Xin-nan Li,Xiang-wen Zhou,Zhen-ming Lu,Jie Zhang,Bing Liu

DOI: https://doi.org/10.14078/j.cnki.1001-3741.2016.01.001

2016-01-01

Abstract:The friction and wear properties of matrix graphite in spherical fuel element for high temperature gas-cooled reactor at different temperatures and loads in helium were studied on a QHT-1000E friction and wear tester. The friction surfaces of matrix graphite were analyzed by scanning electron microscope to investigate the friction mechanism of matrix graphite. There were great differences among the behaviors of matrix graphite at different temperatures in helium. The effect of temperatures on the friction and wear properties of matrix graphite changed with different loads. It was found that, under relatively lower load, matrix graphite exhib-ited relatively greater friction coefficient in the temperature range of 400~700℃,while it presented relatively same lower fiction coef-ficients at other temperatures in helium. On the contrary, matrix graphite demonstrated nearly large friction coefficient in the temper-ature range of 100~200℃and 400~700℃, while the fiction coefficients of matrix graphite were relatively small in the other temper-ature range in helium. Especially under low temperature of 100~200 ℃, load had a great influence on the friction and wear proper-ties of matrix graphite. The recorded friction coefficient of matrix graphite tended to be correlated with the wear loss and was related to the friction mechanism:When the friction coefficient of matrix graphite was relatively large, matrix graphite was dominated by ad-hesive wear and had a correlated large wear loss. When the matrix graphite offered a relatively small friction coefficient, the main wear style was abrasive wear and the correlated wear loss was small in comparison.