Influence of Alloying Elements Partitioning Behaviors on the Microstructure and Mechanical Properties in Alpha Plus Beta Titanium Alloy
Huang Sensen,Ma Yingjie,Zhang Shilin,Qi Min,Lei Jiafeng,Zong Yaping,Yang Rui
DOI: https://doi.org/10.11900/0412.1961.2018.00460
IF: 1.797
2019-01-01
ACTA METALLURGICA SINICA
Abstract:During the thermal treatments of alpha+beta titanium alloys in (alpha+beta) phase field, alloying element partitioning effect takes place accompanying with the alpha <->beta transformation, which results in the segregation of alpha stabilizing elements (Al, O) and beta stabilizing elements (V, Mo, etc.) into the corresponding phases respectively. The element partitioning effect will further affect the microstructure characteristics (phase constitution, microstructure size), plastic deformation modes and the final mechanical properties of the alloy. In this work, the influences of solution temperature and cooling rate on the element partitioning behavior during solution process of Ti-6Al-4V alloy in (alpha+beta) phase field were investigated. The element concentrations in primary alpha phase (alpha(p)) and beta transformed region (beta(t)) were characterized by EPMA technique. The microstructural variation of beta(t) with respect to solution temperature was analyzed. It was found that beta(t) showed an obvious increase of Al content and decrease of V content with the increasing of solution temperature, while the alpha(p) exhibited less noticeable change, which led to the reduction of concentration difference between the two phases. Under the same solution temperature, the microstructures and element distributions at different cooling rates (water quenching, air cooling, furnace cooling) were exhibited. The slow cooling processing especially furnace cooling would induce higher volume fraction of alpha(p) phase and more pronounced element partitioning. The microstructural characteristics of beta(t) cooled from different solution temperatures were further analyzed. During the water or air cooling process, the transformations of beta -> matensite/alpha(s) happened, and the sizes of martensite or alpha(s) were postulated to be dependent on the element concentration of beta phase. The properties of local microstructure (alpha(p), beta(t)) were further measured by nanoindentation. It indicates that the intrinsically anisotropic character of the hexagonal crystal structure (hcp) of the alpha(p) phase has decisive consequences for the properties, while the elastic modulus and hardness of beta(t) calculated by nanoindentation are mainly dominated by the width of alpha(s) lamellas. On the basis of the above results, the relationship between solution temperature, element concentration of local microstructure, microstructure size and mechanical properties of local microstructure was finally discussed.