Mechanical Properties Of A Thermally-Aged Cast Duplex Stainless Steel By In Situ Tensile Test At The Service Temperature

Qingdong Zhang,Sida Ma,Tao Jing

DOI: https://doi.org/10.3390/met9030317

IF: 2.695

2019-01-01

Metals

Abstract:Z3CN20.09M cast duplex stainless steel (CDSS) has been used for primary coolant water pipes in pressurized water reactors due to its excellent mechanical properties. Such pipes operate at an elevated service temperature (similar to 320 degrees C) and experience issues of thermal aging embrittlement. In situ tensile tests were conducted to investigate the deformation mechanisms of Z3CN20.09M CDSS after long-term thermal aging at 475 degrees C for up to 2000 h in both optical microscope and scanning electron microscope at 320 degrees C. For the 320 degrees C tests, the tensile stress and other mechanical properties, e.g. the yield stress and the ultimate tensile strength, increase during the thermal aging process and recover to almost the same level as the unaged condition after annealing heat-treatment, which is caused by the formation and dissolution of precipitation during aging and anneal heat-treatment, respectively. For the slip mechanism, straight slip lines form first in the austenite phase. When these slip lines reach the austenite/ferrite interface, three kinds of slip systems are found in the ferrite phase. During the fracture process, the austenite phase is torn apart and the ferrite phase shows a significant elongation. The role of the ferrite phase is to hold the austenite matrix, thus increasing the tensile strength of this steel.