Abstract:LiTaO3/Al2O3 ceramic composites were fabricated by hot pressing and pressureless sintering, respectively, to investigate the effect of piezoelectric secondary phase on the properties of structural ceramics. Phase constitution, microstructure and mechanical properties of the ceramic composites were studied. LiTaO3 could stably coexist with Al2O3 during sintering. LiTaO3 phase was located at the grain boundaries of Al2O3 matrix fabricated by different processing routes. Domain structures were clearly seen in LiTaO3, confirming that LiTaO3 remained hexagonal ferroelectric phase. About 5 vol.%LiTaO3/Al2O3 ceramic composite prepared by pressureless sintering at 1300°C showed an increase in fracture toughness. Energy dissipation due to domain switching was suggested as a toughening mechanism. With the increasing of LiTaO3 content, the domain switching toughening mechanism was decompensated by the decreased relative density of LiTaO3/Al2O3 ceramic composites. For LiTaO3/Al2O3 ceramic composites prepared by hot pressing at 1500°C, the bending strength decreased because of the increased grain size of Al2O3 matrix. The toughening effect due to domain switching was also decompensated by the coarsening of Al2O3 matrix grains, the weaker net-like LiTaO3 phase and the weaker bonding strength between LiTaO3 phase and Al2O3 matrix.

Non-180 8 domains formation mechanism in LiTaO 3 grains of an Al 2 O 3 / LiTaO 3 composite

Non-180° Domains Formation Mechanism in LiTaO3 Grains of an Al2O3/LiTaO3 Composite

EFFECT OF GRAIN STATE ON DOMAIN STRUCTURE IN LiTaO_3 GRAINS

DOMAIN STRUCTURES IN LiTaO3 PARTICLES DISPERSED IN Al2O3 MATRIX CERAMIC COMPOSITE

Characterization of Domain Configurations in LiTaO3/Al2O3 Ceramic Composites

Effect of grain sizes on domain structures in Al2O3/LiTaO3 composite ceramics

Microstructure and Toughening Mechanisms in an Al2O3 Ceramic Matrix Composite Dispersed with LiTaO3 Particles

Effect of LiTaO3grain Sizes on Microstructure and Properties of Al2O3

Effect of Grain Sizes on Domain Structures in Al_2O_3/LiTaO_3 Composite Ceramics

TEM Characterization of Domain Boundaries in a Ti–46Al–1Cr–0.2Si Alloy

Microstructure and mechanical properties of Al2O3 particle reinforced LiTaO3 piezoelectric ceramic matrix composites

Observation of Ferroelectric Domains in Litao3

Domain structure inversion characterization of near stoichiometric lithium tantalate

Direct Observation of Ferroelectric Domains in LiTa O 3 Using Environmental Scanning Electron Microscopy

Domain Structures and Toughening Mechanism in Al2o3 Matrix Ceramic Composites Dispersed with Piezoelectric Litao3

Domain Structure Moving Characterization of Near-Stoichiometric Lithium Tantalate

Sintering Mechanism and Dielectric Properties of LiTaO3 Matrix Composites with the Addition of Al2O3 Particles

Nanoscale Banded 90 Degrees Domain Patterns In (111) Oriented (Pb,La)Tio3 Thin Films

Hierarchical Domain Structure Of Lead-Free Piezoelectric (Na-1/2 Bi-1/2)Tio3-(K-1/2 Bi-1/2)Tio3 Single Crystals

In Situ TEM Observation of Crack Propagation in LiTaO3 Particle Toughened Al2O3 Ceramics

Ferroelectric Domain Structure of Discrete PbTiO3 Nanograins