Supporting Information Available : Synthesis of WO 3 nanostructures and their ultraviolet photoresponse property

Nengjie Huo,Shengxue Yang,Zhongming Wei,Jingbo Li

2013-01-01

Abstract:Synthesis of WO3 nanostructures We have synthesized WO3 nanostructures such as nanowires, nanorods bundles and nanotubes bundles by a facile hydrhtermal method described as follows: First, two kinds of acid solutions were prepared, one was hydrochloric acid solution (2M) by adding concentrated hydrochloric acid (12M) to de-ionized water with the volume ratio of 1:5, another was citric acid solution (2M) by dissolving citric acid power (12.61 g) into 30 ml de-ionized water. Then sodium tungstate power (0.66 g) was dissolved in 20 ml de-ionized water under vigorous magnetic stirring and then ammonium sulfate (0.53 g) was dissolved in the Na2WO4 solution (a compared experiment was also conducted without (NH4)2SO4), after stirring for 30 min, 2M HCl solution was slowly dropped into the mixed solution under magnetic stirring until the pH value of the solution reached 0.5-2 and then the solution was transferred into a Teflon-lined 50 ml capacity autoclave, and maintained at 180 C for 4 h. After reaction, the autoclave cooled down naturally to room temperature and the precipitate was centrifuged and washed with de-ionized water and absolute ethanol for 2-3 times to remove ions that possibly remained at the final products, then dried at 60 C for 12 h. Meanwhile, another experiment was carried out with 2M citric acid solution as the acidification agent instead of 2M HCl solution to adjust the pH value of solution in the presence of ammonium sulfate while keeping other conditions unchanged.