Hierarchical Structures Novel Three-Dimensional Nanoporous Alumina as a Template for Hierarchical TiO 2 Nanotube Arrays

Daoai Wang,Lianbing Zhang,Woo-Jin Lee,M. Knez,Lifeng Liu

2012-01-01

Abstract:Porous anodic aluminium oxide (AAO), made by electrochemical anodization of aluminium, has been extensively investigated in the past two decades for its widespread applications in the fi eld of nanoscience and nanotechnology. Besides its use as photonic crystals, [ 1 , 2 ] sensors, [ 3 ] bio-separators [ 4 ] and superhydrophobic supports, [ 5 , 6 ] porous AAO is very likely the most commonly used hard template, which allows fabrication of a broad spectrum of 1D nanostructures. [ 7–20 ] In general, the anodization of aluminium has to be carried out under relatively mild conditions with a chemically or electrochemically polished mirror-fi nished Al surface. Any harsh conditions, e.g., an elevated temperature and/or an increased concentration of electrolyte, a high voltage or a rough Al surface, could cause a very high local current fl ow, eventually leading to a catastrophic ‘breakdown’ of the substrate. [ 21–23 ] So far, a few attempts have been made in order to avoid a breakdown during an anodization. [ 24–29 ] For instance, Chu et al. found that aged sulfuric acid helps to improve the critical anodizing potential for a breakdown. [ 24 ] Lee et al. demonstrated that a pre-anodized oxide layer ( > 400 nm) is able to provide uniform pore nucleation sites and therefore effectively suppresses the breakdown during hard or mild anodization in phosphoric acid (H 3 PO 4 ) at a high voltage (e.g., 195 V). [ 26 , 27 ] Nevertheless, a very smooth, mirror-fi nished aluminium surface as well as a low anodizing temperature are still needed in order to avoid failure of anodization under harsh conditions. Particularly, anodization of Al in H 3 PO 4 at