Supporting Information Palladium Nanoparticles with High Energy Facets as a Key Factor of Dissociating O 2 in the Solvent-Free Selective Oxidation of Alcohols

Feifei Wang,Zhansheng Lu,Lin Yang,Yanxing Zhang,Qinghu Tang,Yuming Guo,Xiaoming Ma,Zongxian Yang

2013-01-01

Abstract:Chemicals. Sodium hydroxide (NaOH), glutamate, ethylene glycol, ethanol and sodium borohydride (NaBH 4) were purchased from the China National Pharmaceutical Group Corp. Palladium chloride (PdCl 2 ·2H 2 O) was purchased from Alfa Aesar. Benzyl alcohol (99%), DL-sec-phenethylalcohol (98%), 4-methoxybenzyl alcohol (98%) and cinnamyl alcohol (98%) were all purchased from Beijing Innochem Science & Technology Co., Ltd. Aladdin Reagent Company. All chemicals were analytical grade and were used without further purification. Double distilled water (DD water) was used in all of the experiments. Main experiment for preparation of Pd/F-HAP catalyst. HAP [Ca 10 (PO 4) 6 (OH) 2 ] with a flower-like three dimensional architecture (F-HAP) was successfully prepared through a facile transformation process of hedgehog-like aragonite precursors according to our previous report. 1 A detailed process of catalyst preparation was as follows: an aqueous solution of PdCl 2 (2 mg/mL, 1.5 mL), and glutamate (50 mg) were mixed together in EG (35 mL). The pH of the system was adjusted to ca. 10 by dropwise addition of the 8 wt% NaOH/EG solution under vigorous stirring. During the process, the yellow solution turned into colorless. Subsequently, F-HAP (1g) was added, and the mixture was stirred for 0.5 h to obtain a homogeneous suspension. Upon completion, the suspension was transferred into a 50 mL Teflon-lined stainless steel autoclave.