Effect of B2O3 Addition on Mineralogical Phases and Leaching Behavior of Synthetic CaO–SiO2–MgO–Al2O3–CrOx Slag

Yong Lin,Qingyun Luo,Baijun Yan,Timo Fabritius,Qifeng Shu

DOI: https://doi.org/10.1007/s10163-020-01015-4

2020-01-01

Journal of Material Cycles and Waste Management

Abstract:Boron oxide is frequently applied in modification of stainless steelmaking slag to mitigate the disintegration of slag. In this work, the effect of B 2 O 3 on mineralogical phases and hexavalent chromium leaching behavior of synthetic CaO–SiO 2 –MgO–Al 2 O 3 –CrO x slag was investigated. Di-calcium silicate, merwinite, spinel, akermanite, and matrix phase were observed as main minerals in slags by scanning electron microscope (SEM) equipped with energy-dispersive spectrometry (EDS) and X-ray diffraction (XRD) techniques. It was found that 2% B 2 O 3 addition is sufficient to eliminate the disintegration of synthetic slag by suppressing the phase transition to γ -Ca 2 SiO 4 . The size of spinel phase increases with increasing B 2 O 3 , which could be well interpreted by enhanced Ostwald ripening. The amount of Ca 2 SiO 4 phase in slag was reduced by addition of B 2 O 3 ; however, excess B 2 O 3 (> 2%) addition would significantly increase chromium concentration and overall chromium distribution in Ca 2 SiO 4 phase. Leaching results according to US-EPA-3060A method indicated that excess boron oxide addition (> 2%) leads to a significant increase of hexavalent chromium leaching concentrations and should be avoided for stabilizing stainless steel slag.