Abstract:Mechanical Performance of traditional gas-shielded arc welded joints of 700 MPa grade microalloyed C-Mn steel cannot meet service requirements. Laser welding, with its characteristic high energy density, is known to improve the welding performance of experimental steels. In the present study, Nb-Ti microalloyed steel with a thickness of 4.5 mm was welded using a 4 kW fiber laser. The microstructure, precipitation, and mechanical properties of the welded joints were studied. The hardness and tensile strength of the welded joints were higher than those of the base metal (BM). The microstructure of the fusion zone (FZ) and coarse grain heat affected zone (CGHAZ) was lath martensite (LM), while the microstructure of the fine grain HAZ and mixed grain HAZ consisted of ferrite and martensite/austenite islands. Although LM was observed in both the FZ and CGHAZ, the hardness and calculated tensile strength of the FZ were lower than those of the CGHAZ, due to a reduction in solid solution strengthening by element loss and the dissolution of high-hardness precipitates in FZ. Most precipitates such as [(Nb,Ti)C and (Nb,Ti)(C,N)] that were present in the BM were dissolved, which led to an increase in C and N in solid solution in the FZ. Thus, the elastic modulus of the FZ was higher than that of the BM. Similarly, the elastic modulus of the CGHAZ was higher than that of the BM due to the segregation of C and N atoms during the welding process. The toughness of the FZ was superior to that of the BM, and the toughness of the HAZ approached 91% of that of the BM. The change in toughness primarily depended on the microstructural refinement, the increase in the fraction of grains with high misorientation, the residual austenite in the FZ and CGHAZ, and the dissolution of coarse precipitates.

Temperature Field Simulation and Mechanical Properties of Laser Welded Dp980 Steel Joints

Microstructure- and Strain Rate-Dependent Tensile Behavior of Fiber Laser-Welded DP980 Steel Joint

Experimental and Numerical Study on Local Mechanical Properties and Failure Analysis of Laser Welded Dp980 Steels

Microstructure and Mechanical Properties of Fiber Laser Welded QP980 Steel

Microstructure and Tensile Behavior of Fiber Laser-Welded Blanks of Dp600 and Dp980 Steels

Microstructure and fracture behavior of laser welded joints of DP steels with different heat inputs

Fiber Laser Welding of 1700-MPa, Ultrahigh-Strength Steel

Microstructure Evolution and Mechanical Properties of Laser Welded Dissimilar/Similar Joints Between Medium‐Mn Transformation‐Induced Plasticity Steel and DP980/22MnB5 Steels

Microstructure and Mechanical Properties of Laser Welded Dissimilar Joints Between QP and Boron Alloyed Martensitic Steels

Dissimilar Laser Welding/Brazing of 5754 Aluminum Alloy to DP 980 Steel: Mechanical Properties and Interfacial Microstructure

Mirostructure and Properties of Laser Welded Joints of Dual Phase and Press-Hardened Steels

Microstructure and Properties in Dissimilar/similar Weld Joints Between DP780 and DP980 Steels Processed by Fiber Laser Welding

Tensile resistance, microstructures of intermetallic compounds, and fracture modes of welded steel/aluminum joints produced using laser lap welding

Effect of Heat Input on Microstructure and Mechanical Properties of Laser Welded Medium Mn Steel Joints

Microstructural evolution and mechanical properties of laser-welded joints of medium manganese steel

Microstructure and Performance of Hybrid Laser-Arc Welded 40 Mm Thick 316 L Steel Plates

Research on Microstructure and Mechanical Properties of Fiber Laser Lap Welded Joints of 22Mn B5 Ultra-high Strength Steel

Influence of hot forming on microstructure and mechanical properties of laser tailor-welded dissimilar ultra-high-strength steels

Microstructure-Property Correlations in Fiber Laser Welded Nb-Ti Microalloyed C-Mn Steel

A Study of the Performance of Dissimilar Pulsed-Laser-Welded JSC590R/JAC980YL Steel Joints of Differential Thickness

Formation, microstructure and mechanical properties of double-sided fiber laser welded ultra-high strength steel