Comparative Study on Optical Properties and Scratch Resistance of Nanocomposite Coatings Incorporated with Flame Spray Pyrolyzed Silica Modified Via In-Situ Route and Ex-Situ Route

Yun Wang,Ling Zhang,Yanjie Hu,Chunzhong Li

DOI: https://doi.org/10.1016/j.jmst.2015.11.008

2015-01-01

Journal of Material Science and Technology

Abstract:A new type of transparent scratch resistant coatings including in-situ modified SiO 2 （g-SiO 2 ） in flame spray pyrolysis（FSP） process was prepared. The maximum content of g-SiO 2 in the coating was 15 wt%, which is higher than that of SiO 2 modified by traditional wet chemical route（l-SiO 2 , only 10 wt%）. The results of transmission electron microscopy have demonstrated that in-situ surface modified g-SiO 2 particles dispersed well with smaller agglomerates in the final coating, which was much better than the particles modified via wet chemical route. Visible light transmittance and haze tests were introduced to characterize the optical quality of the films. All coatings were highly transparent with the visible light transmittance of above 80%, especially for coatings containing g-SiO 2 , which exhibited slightly higher visible light transmittance than l-SiO 2 embedded one. The haze value of coatings incorporated with 15wt% g-SiO 2 was 1.85%, even lower than the coating with 5 wt% l-SiO 2 （haze value of 2.09%）, indicating much better clarity of g-SiO 2 . The excellent optical property of g-SiO 2 filled coatings was attributed to the good dispersion and distribution of particles. Nano-indention and nano-scratch tests were conducted to investigate the scratch resistance of coatings on nano-scale. The surface hardness of the coatings rose by 18% and 14%, and the average friction coefficient decreased by 15% and 11%, respectively, compared to the neat coat due to the addition of 10 wt% g-SiO 2 and l-SiO 2 . The pencil hardness of the coating with 15 wt% g-SiO 2 increased from 2B for the neat coating to 2H. However, the pencil hardness of coating with 10 wt% l-SiO 2 was only H. The results showed that the g-SiO 2 embedded coatings exhibited higher scratch resistance and better optical properties.