A Novel Colloid Composited with Polyacrylate and Nano Ferrous Sulfide and Its Efficiency and Mechanism of Removal of Cr(VI) from Water.

Youru Yao,Na Mi,Cheng He,Yong Zhang,Li Yin,Jing Li,Wei Wang,Shaogui Yang,Huan He,Shiyin Li,Lixiao Ni
DOI: https://doi.org/10.1016/j.jhazmat.2020.123082
IF: 13.6
2020-01-01
Journal of Hazardous Materials
Abstract:Nano ferrous sulfide (n-FeS) colloids show an excellent performance in the application of remediation in situ soil and groundwater. However, due to the interfacial effect and high reactivity of the nano sized FeS, n-FeS easy to agglomerate, which reduces their remediation efficiency. In this study, a novel composite colloid was synthesized using polyacrylic acid salt (PAA) and n-FeS. The PAA-n-FeS colloid was used to remove Cr(VI) in water remediation, and its removal mechanism and efficiency were explored. The results showed that the hydrodynamic diameter of PAA-n-FeS ranged from 65.04-90.09 nm and the zeta potential was from -27 to -54 mV at pH varying from 4.5-9.0. PAA was coated on the surface of n-FeS, which improved the dispersibility and stability of n-FeS by increasing the steric hindrance and electrostatic repulsion between n-FeS particles. Moreover, the Cr(VI) maximum removal amount PAA-n-FeS was 432.79 mg/g, which was significantly higher than that of n-FeS (218.29 mg/g) and PAA (12.32 mg/g). The mechanism of PAA-n-FeS removal of Cr(VI) was mainly derived from its own reducibility. The reaction products were mainly Cr(OH)3, Cr(III)-Fe(III), Cr2O3, and Cr2S3. This research not only finds a new stabilizer for preventing n-FeS agglomeration, but also provides a novel n-FeS composited colloid for promoting the practical application to Cr(VI) removal from water.
What problem does this paper attempt to address?