Abstract:Metallic biomaterials, such as stainless steels, cobalt–chromium–molybdenum (Co–Cr–Mo) alloys, and titanium (Ti) alloys, have long been used as load-bearing implant materials due to their metallic mechanical strength, corrosion resistance, and biocompatibility. However, their magnetic susceptibility and elastic modulus of more than 100 GPa significantly restrict their therapeutic applicability. In this study, spinodal Zr 60 Nb 40 , Zr 50 Nb 50 , and Zr 40 Nb 60 (at.%) alloys were selected from the miscibility gap based on the Zr–Nb binary phase diagram and prepared by casting, cold rolling, and aging. Their microstructure, mechanical properties, corrosion resistance, magnetic susceptibility, and biocompatibility were systematically evaluated. Spinodal decomposition to alternating nanoscale Zr-rich β 1 and Nb-rich β 2 phases occurred in the cold-rolled Zr–Nb alloys during aging treatment at 650°C. In addition, a minor amount of α phase was precipitated in Zr 60 Nb 40 due to the thermodynamic instability of the Zr-rich β1 phase. Spinodal decomposition significantly improved the mechanical strength of the alloys due to nanosized dual-cubic reinforcement. The Zr–Nb alloys showed an electrochemical corrosion rate of 94-262 nm per year in Hanks' solution because of formation of dense passive films composed of ZrO 2 and Nb 2 O 5 during the polarization process. The magnetic susceptibilities of the Zr–Nb alloys were significantly lower than those of commercial Co–Cr–Mo and Ti alloys. The cell viability of the Zr–Nb alloys was more than 98% toward MC3T3-E1 cells. Overall, the spinodal Zr–Nb alloys have enormous potential as bone-implant materials due to their outstanding overall mechanical properties, extraordinary corrosion resistance, low magnetic susceptibility, and sufficient bicompatibility. Statement of significance This work reports on spinodal Zr–Nb alloys with heterostructure. Spinodal decomposition significantly improved their mechanical strength due to the nanosized dual-cubic reinforcement. The Zr–Nb alloys showed large corrosion resistance in Hanks' solution because of formation of dense passivation films composed of ZrO 2 and Nb 2 O 5 during the polarization process. The magnetic susceptibilities of the Zr–Nb alloys were significantly lower than those of commercial Co–Cr–Mo and Ti alloys. The cell viability of the Zr–Nb alloys was more than 98% toward MC3T3-E1 cells. The results demonstrate that spinodal Zr–Nb alloys have enormous potential as bone-implant materials due to their outstanding overall mechanical properties, high corrosion resistance, low magnetic susceptibility, and sufficient biocompatibility.

Co‐extrusion of Nb–1Zr Powder for the Production of a Biocompatible High‐Strength Material for Dental Implants

Nanostructured Ti-13Nb-13Zr alloy for implant application-material scientific, technological, and biological aspects

Development and properties of dental Ti–Zr binary alloys

Nb-Ti-Zr Alloys for Orthopedic Implants

Development and Characterization of Β‐type Ti‐Zr‐Nb‐Sn Dental Implant Materials

Development and characterization of beta-type Ti-Zr-Nb-Sn dental implant materialsEntwicklung und Charakterisierung von Implantatwerkstoffen aus beta-TiZrNbSn-Dentallegierung

Development of Ti-10Nb alloy by powder metallurgy processing route for dental application

Effect of Niobium Content on the Microstructure and Young's Modulus of Ti-xNb-7Zr Alloys for Medical Implants.

Elaboration of Ti-based Biocompatible Alloys Using Nb, Fe and Zr as Alloying Elements

Porous functionally graded material based on a new Ti‐25Nb‐5Zr‐(2Sn) alloy produced using the powder metallurgy technique

Porous niobium coatings fabricated with selective laser melting on titanium substrates: Preparation, characterization, and cell behavior

New Zr-25Ti-xMo alloys for dental implant application: Properties characterization and surface analysis.

Microstructure and Mechanical Behavior of Metal Injection Molded Ti–Nb Binary Alloys As Biomedical Material

Novel Biocompatible Zr-Based Alloy with Low Young’s Modulus and Magnetic Susceptibility for Biomedical Implants

Novel Biocompatible Zr-Based Alloy With Low Young'S Modulus And Magnetic Susceptibility For Biomedical Implants

Biocompatible Magnesium Alloy ZNdK100—Adaptation of Extrusion Parameters to Tailor the Mechanical Properties to Different Implant Applications

Mechanical and biological properties of Ti–(0–25 wt%)Nb alloys for biomedical implants application

Β-Type Zr–Nb–Ti Biomedical Materials with High Plasticity and Low Modulus for Hard Tissue Replacements

Ultrafine-grained Nb-Cu Immiscible Alloy Implants for Hard Tissue Repair:Fabrication,characterization,and in Vitro and in Vivo Evaluation

Spinodal Zr–Nb alloys with ultrahigh elastic admissible strain and low magnetic susceptibility for orthopedic applications

Titanium-Zirconium Binary Alloy as Dental Implant Material: Analysis of the Influence of Compositional Change on Mechanical Properties and In Vitro Biologic Response.