Abstract:High-temperature permanent magnets have an important application in the aerospace and other high-tech fields, among which 2:17-type SmCo magnets have become the first choice for high-temperature permanent magnets due to the strong magnetic anisotropy and high Curie temperature. Although there are studies on the effect of Fe on the remanence and coercivity, the role that Fe plays on coercivity mechanism of SmCo magnets is still unclear. In this work, Sm(CobalFexCu0.08-0.10Zr0.03-0.033) z (x= 0.10-0.16, z=6.90 and 7.40) magnets are prepared and the magnetic properties under different temperatures are investigated. The magnets with an intrinsic coercivity of 603.99 kA/m and a maximum energy product of 87.30 kJ/m(3) at 500 degrees C. are obtained. It is revealed that at room temperature the coercivity of the magnets increases with increasing Fe content, however, at 500 degrees C. the coercivity shows an opposite dependency on Fe content. Moreover, the effect of Fe on coercivity is more obvious at low z value. The phase structure and composition analyses were characterized by XRD and TEM. The results show that with the increase of Fe content, the size of the 2: 17R cell phase increases, the volume ratio of cell boundary 1: 5H phase decreases, and furthermore, both Fe content in the 2: 17R phase and Cu content in the 1: 5H phase increase. The variations of Fe and Cu contents in both phases lead to the change of the domain wall energy difference. With the increase of Cu content of 1:5H phase, the domain wall energy of 1: 5H phase (gamma(1:6)) drops faster at room temperature, the coercivity is determined by gamma(2:17)-gamma(1:5), so the coercivity increases with increasing Fe content. While at 500 degrees C, due to gamma(1:6) at its Curie temperature, the coercivity is mainly determined by the domain wall energy of 2: 17R phase (gamma(1:17)), which decreases with increasing Fe content. The increase of Fe content at the low z value results in a smaller growth of cell size, which leads to a more significant change in coercivity.

First-principles Study of Site Preferences for Fe in Sm(CoFeCuZr)z Permanent Magnets

Preparation and Magnetic Properties of Zn–Cu–Cr–Sm Ferrite Via a Rheological Phase Reaction Method

Effect of Fe on Microstructure and Coercivity of Smco-Based Magnets

Enhanced Magnetic Performance of Fe-rich Sm2Co17-type Magnets by Optimizing Zr Content

Phase separation and chemistry evolution in Fe-rich Sm(CobalFe0.31Cu0.07Zr0.025)7.7 magnets: The effect of initial defect

Phase Separation and Chemistry Evolution in Fe-Rich Sm(Co Balfe 0.31cu 0.07zr 0.025) 7.7 Magnets: the Effect of Initial Defect

First principles study of transition-metal substitutions in Sm–Co permanent magnets

Chemical Segregation Mechanism and Magnetic Properties of Sm2Co17-based Permanent Magnets: Experimental Investigation and First-Principles Calculations

Atomic-scale Structure Clarification of the Planar Z Phase and Its Influence on the Magnetic Properties in Sm(CoFeCuZr)z Permanent Magnets

Atomic-scale structure clarification of the planar Z phase and its influence on the magnetic properties in Sm(CoFeCuZr) permanent magnets

Mechanism Research of Z Value Affecting Magnetic Properties of Sm(CoFeCuZr)(z)

Correlation between ordered solid solution and cellular structure of Sm2Co17 type magnets with high iron content

Quantitative analysis of pinning-hardened intrinsic coercivity of Sm(CoFeCuZr)z (z = 7.0–7.8) high-temperature permanent magnets

Magnetic properties of (Sm, Zr)(Fe, Co)10−xTix (x = 0, 0.5, 1) bulk magnets

Microstructure and Magnetic Properties of Sm(CobalFexCu0.049Zr0.024)7.5 (x=0.102～0.282)

First-Principles Calculations on Structural and Magnetic Properties of SmCo 3 Alloys Doped with Transition Metal Elements

Fe content influence on the microstructure of solution-treated Sm-Co-Fe-Cu-Zr alloys

Thermodynamics and Magnetism of SmFe12 Compound Doped with Zr, Ce, Co and Ni: An Ab Initio Study

Influence of 1:7 H phase stability on the evolution of cellular microstructure in Fe-rich Sm-Co-Fe-Cu-Zr magnets

Formation of Semi-Coherent Zr-rich Lamellar Phase in 2:17-Type Sm-Co-Fe-Cu-Zr Magnets with High Fe Content

Cell-boundary-structure controlled magnetic-domain-wall-pinning in 2:17-type Sm-Co-Fe-Cu-Zr permanent magnets