Abstract:The 2195 Al-Cu-Li alloy is widely utilized in the aerospace industry due to its lightweight nature and high strength. Consequently, gaining a comprehensive understanding of techniques to enhance its microstructural and mechanical properties is crucial for the consistent production of reliable and high-strength aerospace components. In this investigation, a pristine 2195 industrial ingot was subject to three distinct forging pretreatments: PT1, which involved a direct three upsetting and three stretching (3U3S) process; PT2, which combined double stage homogenization (DH) with 3U3S; and PT3, which involved DH along with six upsetting and six stretching (6U6S). Subsequent warm deformation and T8 aging treatment were applied to the pretreated forgings. The microstructure evolution during the processes and the final mechanical properties in three orthogonal dimensions were examined. The findings revealed that the combination of DH and multi-dimensional forging (MDF) facilitated the dissolution of non-equilibrium phases to a greater extent. Consequently, the main strengthening phase transformed from the T 1 + δ` phase observed in PT1 to the denser T1 + little θ` phase observed in PT2 and PT3 after T8 aging treatment. Notably, the tensile strength and yield strength of PT2 and PT3 specimens increased by 20-30 MPa in all three directions. Moreover, the MDF process accelerated the recrystallization behavior from PT1 to PT3, resulting in a gradual reduction in the average grain size of the pretreated samples from 356 μm to 186 μm. Following warm forging and T8 aging, the grains exhibited a finer and equiaxed structure. Additionally, the coarse phase was identified as the primary source of transgranular cracking. The coarse phases within the matrix became more homogeneous and finer from PT1 to PT3, with a gradual decrease in their area fraction. On the fracture surfaces, the aggregation of coarse phases diminished. Consequently, the elongation in the z-direction improved, and the elongation anisotropy and standard deviation decreased in all three directions for PT3 specimens. The findings presented in this study provide valuable insights into the high-performance manufacturing of Al-Cu-Li alloys.

Tuning microstructure and mechanical properties of squeeze-cast whisker-reinforced 2024Al composites by hot forging process design

Effect of Forging on the Microstructure and Tensile Properties of 2024al/al18b4o33w Composite

Effect of whisker breakage on the forgeability and the tensile properties of the forged 2024Al/Al 18 B 4 O 33 w composite

Increased Hot Forgeability of 2024al/al18b4o33w Whisker Composites at High Strain Rates

Effect of the Aspect Ratio of Whisker on Work Hardening Rate of As Forged 2024al/al18b4o33w Composite

Microstructure and Mechanical Properties of ABOw and Nickel-Coated MWCNTs Reinforced 2024al Hybrid Composite Fabricated by Squeeze Casting

Experimental and theoretical investigation on the compressive behavior of aluminum borate whisker reinforced 2024Al composites

Study on Hot Deformation Behavior and Workability of Squeeze-Cast 20 Vol%sicw/6061al Composites Using Processing Map

Hot Deformation Behaviors of Bi2O3-coated Al18B4O33 Whisker Reinforced Aluminum Matrix Composite with High Formability

High strength-ductility synergy of MgAlB4 whisker reinforced aluminum matrix composites achieved by in situ synthesis

Research on the Secondary Forgeability of High Volume Fraction Whisker Reinforced Aluminum Matrix Composites of Original Squeeze Casting

Effects of multi-directional forging on the microstructure and mechanical properties of TiB2 particulate reinforced 6061Al composite

Improving strain hardening behavior in nano-intermetallic reinforced aluminum in-situ composites through an optimized twostep thermal processing method; sintering and uniaxial forging

A Study of Hot Rolling of 6061 Aluminum Alloy Matrix Composite Reinforced with SnO2-coated Al18B4O33 Whisker

Tensile Properties of an Aluminum Matrix Composite Reinforced by Sno2-Coated Al18b4o33 Whisker

Influence of Forging Temperature on the Microstructures and Mechanical Properties of a Multi-Directionally Forged Al–Cu–Li Alloy

Microstructure, texture and mechanical properties of 0.4GNPs‐Mg‐8Al‐1Sm composites prepared by pulse current‐assisted multi‐directional forging

Effect of forging pretreatment on the microstructures and mechanical properties of the Al-Cu-Li alloy

Effect Of Hot-Deformation On Microstructure And Mechanical Properties Of (Sicw Center Dot Sicp)/2024al Hybrid Nanocomposites

High Temperature Mechanical Behavior and Microstructure of α-Si 3N4w/4032Al Composite Fabricated by Squeeze Casting

High temperature mechanical behavior and microstructure of alpha-Si(3)N(4)w/4032Al composite fabricated by squeeze casting