Abstract:A novel addition-curable novolac resin with phthalonitrile groups (PN) was successfully synthesized by a simple nucleophilic substitution reaction between the novolac resin and 4-nitrophthalonitrile. The final product was characterized with gel permeation chromatography (GPC), Fourier transform infrared (FT-IR) spectrometry, and proton nuclear magnetic resonance ( 1 H-NMR) spectroscopy. Processing capability and cure behavior of PN resin was investigated by rheometer and differential scanning calorimetry (DSC), respectively. Rheometric studies showed PN resin possessed a broad processing window between 140 and 225°C with a low viscosity from 0.4 to 4 Pa.s. DSC results showed PN resin can be cured at about 220°C via thermal polymerization of phthalonitrile groups. An ultrahigh curing temperature (such as 375°C) that was typical for the other phthalonitrile functional prepolymers was not necessary for this resin and 250°C was used as a maximum post-cure temperature to achieve the desired properties. Thermogravimetric analysis (TGA) showed T 5 % (temperature of 5% weight loss) of the final cured products in nitrogen was 448.7°C, and the char yield was 70.29% at 900°C. Furthermore, T 5% of cured PN resin in air was 455.2°C, and the char yield in air was 34.48% at 700°C,revealing that the cured resin possessed excellent thermo-oxidative stability. Dynamic mechanical analysis (DMA) showed the inflection point of tan δ was 371.9°C. The excellent processability and thermal stabilities proved PN resin as a promising candidate for advanced composite matrices.

Preparation and Characterization of Phthalonitrile Resin Within Hyperbranched Structure

Crosslinkable Hyperbranched Poly(arylene Ether Nitrile) Modifier for Phthalonitrile Resins: Synthesis, Chain-End Functionalization and Properties

Synthesis and Characterization of Hyperbranched Poly(Aryl Ether Ketone) Terminated with Phthalonitrile Group

Boron-containing Phthalonitrile Resin: Synthesis, Curing Behavior, and Thermal Properties

A Pyridazine-Containing Phthalonitrile Resin for Heat-Resistant and Flame-Retardant Polymer Materials

Enhanced thermal property via tunable bisphenol moieties in branched phthalonitrile thermoset

Synthesis, characterization and self-promoted cure behaviors of a new phthalonitrile derivative 4-(4-(3, 5-diaminobenzoyl) phenoxy) phthalonitrile

Thermally stable phthalonitrile resins based on multiple oligo (aryl ether)s with phenyl-s-triazine moieties in backbones

Synthesis and properties of a novel high-temperature vinylpyridine-based phthalonitrile polymer

Branched Phenyl‐s‐triazine Moieties to Enhance Thermal Properties of Phthalonitrile Thermosets

Preparation and properties of high-temperature resistant bisphthalonitrile resins containing trifluoromethyl groups reinforced by poly (aryl ether nitrile) capped by phthalonitrile and composites

Synthesis, Curing Kinetics, and Properties of a Novel Phthalazine‐Based Phthalonitrile Resin

Synthesis and Characterization of Phthalonitrile Prepolymers Cured with 2,6-Bis(4-aminophenoxy)benzonitrile

High-Performance Boron-containing Phthalonitrile Resins

Catalytic Polymerization of Phthalonitrile Resins by Carborane with Enhanced Thermal Oxidation Resistance: Experimental and Molecular Simulation

Enhanced properties of phthalonitrile resins reinforced by novel phthalonitrile-terminated polyaryl ether nitrile containing fluorene group

Synthesis and Properties of Phthalonitrile Terminated Polyaryl Ether Nitrile Containing Fluorene Group

Preparation and characterization of a high heat resistant phthalonitrile resin modified by polyborosilazane ceramic precursor

Enhanced Thermal Properties of Phthalonitrile Networks by Cooperating Phenyl-S-triazine Moieties in Backbones

Synthesis, polymerization, and properties of the allyl‐functional phthalonitrile

Addition-curable phthalonitrile-functionalized novolac resin