Abstract:Nitrogen-containing mesoporous carbon with different specific surface areas and pore volumes were prepared by using colloidal silica spheres as the hard template, chitosan as a carbon precursor, and ZnCl2 as activation agent. The morphology, surface area, and pore structure of the prepared carbons were characterized by different techniques. The influence of the ratio of silica to chitosan and the use of ZnCl2 on the pore volume and surface area of porous carbon materials were explored. It was found that the nitrogen-doped mesoporous carbon (CSi-1.75) without using activation agent showed lowest surface area but the pore volume can reach up to 4.53 cm(3)center dot g(-1). The carbon (CSi-1.75-Zn) prepared by using ZnCl2 as activation agent, had the larger surface area (1 032 m(2)center dot g(-1)) and the pore volume decreased to 1.99 cm(3)center dot g(-1) and had more pyridine-nitrogen and pyrrole-nitrogen. In the three electrodes with 6.0 mol center dot L-1 KOH as the electrolyte, when the current density was 0.5 A center dot g(-1), the specific capacitance of CSi-1.75-Zn can reach 344 F center dot g(-1), while the specific capacitance of CSi-1.75 was only 255 F center dot g(-1). This indicates that the surface area of the carbon material had the greatest impact on the supercapacitive performance. The capacitance contribution analysis results showed that both the double-layer capacitance and pseudo capacitance of CSi-1.75-Zn were improved compared with CSi-1.75, indicating that larger specific surface area and more pyridine-nitrogen and pyrrole-nitrogen are conducive to improving the capacitance of carbon materials.

Study on the Preparation and Mechanism of Chitosan-Based Nano-Mesoporous Carbons by Hydrothermal Method.

Facile and eco-friendly synthesis of chitosan-based mesoporous carbon for adsorbent

Preparation of Free-Standing High Quality Mesoporous Carbon Membranes

Mesoporous Carbon Materials: Synthesis and Modification.

Preparation of Mesoporous Carbons from Acrylonitrile-methyl Methacrylate Copolymer/Silica Nanocomposites Synthesized by In-Situ Emulsion Polymerization

Facile synthesis of hollow carbon nanospheres from hollow chitosan nanospheres.

Preparation and application performance study of biomass-based carbon materials with various morphologies by a hydrothermal/soft template method

Design of Carbon Materials with Ultramicro-, Supermicro- and Mesopores Using Solvent- and Self-Template Strategy for Supercapacitors

Preparation of Chitosan Bicomponent Nanofibers Filled with Hydroxyapatite Nanoparticles Via Electrospinning

Preparation and Structure of Polyacrylonitrile-based Mesoporous Carbon via Inorganic Template Method

Facile Synthesis of Ordered Mesoporous Carbons with High Thermal Stability by Self-Assembly of Resorcinol-Formaldehyde and Block Copolymers under Highly Acidic Conditions

A Direct Synthesis of Mesoporous Carbons with Bicontinuous Pore Morphology from Crude Plant Material by Hydrothermal Carbonization

Preparation of Porous Carbons from Halloysite-Sucrose Mixtures

Synthesis of Mesoporous Carbon Using Halloyiste As Template

Preparation and characterization of vinylidene chloride copolymer/nanometer hydrotalcite composites and porous carbons

Synthesis of mesoporous carbon nanosheets using tubular halloysite and furfuryl alcohol by a template-like method

A Simple Method for the Synthesis of High Surface Area Mesoporous Carbon Monolith via Soft Template Technique

An Investigation on the Preparation of Porous Carbons with Zeolite Minerals As Templates

Preparation and electrochemical performance for supercapacitors of chitosan.based porous carbon materials

Preparation and Properties of Multi-Walled Carbon Nanotube/carbon/polystyrene Composites

Oxidation modification of chitosan-based mesoporous carbon by soft template method and the adsorption and release properties of hydroxycamptothecin