Fabrication of a Leaf-Like Superhydrophobic CuO Coating on 6061al with Good Self-Cleaning, Mechanical and Chemical Stability

Zhexin Lv,Sirong Yu,Kaixing Song,Xue Zhou,Xiaoli Yin

DOI: https://doi.org/10.1016/j.ceramint.2020.03.013

IF: 5.532

2020-01-01

Ceramics International

Abstract:Copper oxide is widely used to obtain superhydrophobic surfaces due to its special micro/nano-structures and properties. However, there are few studies on a leaf-like CuO superhydrophobic coating by direct thermal oxidation of Cu on 6061Al substrate. In this work, there is a simple and low-cost method including chemical replacement, thermal oxidation and low-energy-modification with stearic acid. The resultant coating is super-hydrophobic and oleophilic with water contact and sliding angles of 157. 3 degrees +/- 0. 5 degrees and 3. 6 degrees +/- 1, respectively. Additionally, it has low adhesion and excellent self-cleaning performances, whose corresponding mechanical analyses are conducted to theoretically discuss that stable micro/nano-structures and trapped air pockets could effectively influence the interfacial adhesion. Importantly, after tape-peeling, sandpaper-abrasion, and chemical stability tests, the coating still keeps superhydrophobic. Especially, in 3.5 wt% NaCl aqueous solution, compared with the corrosion current density of bare 6061Al substrate (7.18 x 10(-7)A/cm(2)), that of the SHP CuO coating (0.77 x 10(-7)A/cm(2)) decreases obviously. In sum, the method is especially suitable for large-scale industrial production of a stable superhydrophobic coating on Al alloys.