Facile Synthesis of Manganese Oxide Nanostructures with Different Crystallographic Phase and Morphology for Supercapacitors

Yankai Yuan,Jingyi Zhu,Ying Wang,Shuni Li,Pujun Jin,Yu Chen

DOI: https://doi.org/10.1016/j.jallcom.2020.154524

IF: 6.2

2020-01-01

Journal of Alloys and Compounds

Abstract:The charge storage performances of manganese oxide (MnO2) nanostructures highly depend on their crystallographic phase and structure. In this work, MnO2 nanostructures (alpha-MnO2, beta-MnO2 and delta-MnO2) with high crystallinity and different morphology are prepared through a simple, mild and controllable hydrothermal method at 120 degrees C. [Mn(C8H4O4) (H2O)(2)](n), a water insoluble metal-organic framework (Mn-MOF), can efficiently react with KMnO4 at different pH, which results in the generation of alpha-MnO2, beta-MnO2 and delta-MnO2. The size of MnO2 nanostructures can be easily adjusted by controlling the ratio of Mn(II)/Mn(VII). The as-prepared MnO2 nanostructures with different structures and sizes are characterized by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM), X-ray photoelectron spectroscopy (XPS), and N-2 adsorption/desorption. Among three samples, the layered delta-MnO2 nanostructures with Mn(II)/Mn(VII) = 2.0 show a specific surface area of 240 m(2). g(-1), specific capacitance of 416 F.g(-1) at 0.5 A.g(-1), which can be explained as both adsorption/desorption and intercalation/ deintercalation process. The energy density of the asymmetric supercapacitor constructed by MnO2 and activated carbon (AC) is 23.2 W. h.kg(-1) at a power density of 425 W.kg(-1). The controllable synthesis of MnO2 nanostructures with different crystallographic phases based on Mn-MOF may give further insights into supercapacitors. (C) 2020 Elsevier B.V. All rights reserved.