Abstract:Tensile, compressive, cyclic tension-tension, and cyclic compression-compression tests at room temperature were systematically applied to a Zr52.5Cu17.9Al10Ni14.6Ti5 bulk metallic glass for comprehensive understanding of its damage and fracture mechanisms. Under tensile loading, the metallic glass only displays elastic deformation followed by brittle shear fracture. Under compressive loading, after elastic deformation, obvious plasticity (0.5 to 0.8 pct) can be observed before the final shear fracture. The fracture strength under compression is slightly higher than that under tension. The shear fracture under compression and tension does not occur along the maximum shear stress plane. This indicates that the fracture behavior of the metallic glass does not follow the Tresca criterion. The fracture surfaces show remarkably different features, i.e., a uniform vein structure (compressive fracture) and round cores coexisting with the radiating veins (tensile fracture). Under cyclic tension-tension loading, fatigue cracks are first initiated along localized shear bands on the specimen surface, then propagated along a plane basically perpendicular to the stress axis. A surface damage layer exists under cyclic compression-compression loading. However, the final failure also exhibits a pure shear fracture feature as under uniaxial compression. The cyclic compression-compression fatigue life of the metallic glass is about a factor of 10 higher than the cyclic tension-tension fatigue life at the same stress ratio. Based on these results, the damage and fracture mechanisms of the metallic glass induced by uniaxial and cyclic loading are elucidated.

Fatigue Behavior of A Minor Yttrium Doped ZrCuNi-Based Metallic Glass Alloy Fabricated by Industrial Grade Raw Material

Fatigue Behavior of a High-Toughness Zr 61 Ti 2 Cu 25 Al 12 Bulk Metallic Glass

Tension-Tension Fatigue Behavior of High-Toughness Zr61Ti2Cu25Al12 Bulk Metallic Glass

Improving fatigue property of Zr–Ni–Al metallic glass by tailoring chemical composition with high structure stability

Fatigue Endurance Limit and Crack Growth Behavior of a High-Toughness Zr 61 Ti 2 Cu 25 Al 12 Bulk Metallic Glass

Fatigue and fracture behavior of bulk metallic glass

Mechanical Properties of Monolithic Zr62Al8Ni13Cu17 Bulk Metallic Glass

Stress-life fatigue behavior and fracture-surface morphology of a Cu-based bulk-metallic glass

Fracture and fatigue behaviour of a laser additive manufactured Zr-based bulk metallic glass

Quasi-static and dynamic compressive behavior of Zr-based bulk metallic glass with yttrium addition

Compression-compression Fatigue Behavior of CuZr-based Bulk Metallic Glass Composite Containing B2 Phase

Crack-Resistance Curve of A Zr-Ti-Cu-Al Bulk Metallic Glass with Extraordinary Fracture Toughness

Investigation of Deformation Behavior of Zr-Ti-Ni-Cu-Be Bulk Metallic Glass Containing Nanocrystals

Thermal Stability and Mechanical Properties of Zr50Ti5Cu18Ni17Al10 Bulk Metallic Glass

Incorporation of ultrafine nanograins in Zr–Cu–Al–Ni–Co bulk metallic glass enabling significantly improved mechanical properties

Glass-Forming Ability, Mechanical Properties, and Energetic Characteristics of ZrCuNiAlNbHfY Bulk Metallic Glasses

Damage-Tolerant Zr-Cu-Al-Based Bulk Metallic Glasses with Record-Breaking Fracture Toughness

Mechanical Properties for a Series of Zr-based Bulk Metallic Glasses

Ultrasonic Fatigue of Ti&lt;sub&gt;40&lt;/sub&gt;Zr&lt;sub&gt;10&lt;/sub&gt;Cu&lt;sub&gt;34&lt;/sub&gt;Pd&lt;sub&gt;14&lt;/sub&gt;Sn&lt;sub&gt;2&lt;/sub&gt; Glassy Alloy

The Crack Initiation Mechanism of the Forged Mg-Zn-Y-Zr Alloy in the Super-Long Fatigue Life Regime

A Novel Ni-Free Zr-Based Bulk Metallic Glass with High Glass Forming Ability, Corrosion Resistance and Thermal Stability