Elimination of Grain Boundaries and Its Effect on the Properties of Silicon Nitride Ceramics

Feng Hu,Tianbin Zhu,Zhipeng Xie,Jian Liu,Zunlan Hu,Di An

DOI: https://doi.org/10.1016/j.ceramint.2020.02.024

IF: 5.532

2020-01-01

Ceramics International

Abstract:To eliminate the excess grain boundary phase in silicon nitride ceramics prepared through hot pressing and a post-sintering heat treatment, carbon was introduced into the sintered ceramics. This was accomplished in two ways: first, a small amount of carbon was used as a sintering additive; however, this creates large pores in the ceramics, resulting in a decrease in the thermal conductivity and mechanical properties of the samples. Alternatively, the C/Si3N4 power bed could be used instead of the BN/Si3N4 power bed, which obviously eliminates the grain boundary phase. Further, the C/Si3N4 power bed possess excellent mechanical properties while increasing the thermal conductivity of the samples. Therefore, the silicon nitride ceramics with 123 W m(-1) K-1 thermal conductivity and 986 MPa bending strength of can be obtained using the C/Si3N4 powder bed during the post-sintering heat treatment.