MoS 2 decorated carbon fiber yarn hybrids for the development of freestanding flexible supercapacitors
José Tiago Carvalho,Afonso Correia,Neusmar J. A. Cordeiro,João Coelho,Sidney A. Lourenço,Elvira Fortunato,Rodrigo Martins,Luís Pereira
DOI: https://doi.org/10.1038/s41699-024-00448-x
IF: 10.516
2024-03-13
npj 2D Materials and Applications
Abstract:Academic and industrial efforts have focused on developing energy storage devices for wearable and portable electronics using low-cost, scalable, and sustainable materials and approaches. In this work, commercially available stretch-broken carbon fiber yarns (SBCFYs) were hybridized with mixed phases of 1 T and 2H MoS 2 nanosheets via conventional and microwave-assisted heating (CAH, MAH) without the use of binders to fabricate symmetric freestanding 1D fiber-shaped supercapacitors (FSCs). Electrochemical characterization performed in a three-electrode configuration showed promising results with specific capacitance values of 184.41 and 180.02 F·g −1 , at 1 mV·s −1 for CAH and MAH, respectively. Furthermore, after performing 3000 CV cycles at 100 mV·s −1 , the capacitance retention was 79.5% and 95.7%, respectively. Using these results as a reference, symmetric 1D FSCs were fabricated by pairing hybridized SBCFYs with MoS 2 by MAH. The devices exhibited specific capacitances of approximately 58.60 ± 3.06 F·g −1 at 1 mV·s −1 and 54.81 ± 7.34 F·g −1 at 0.2 A·g −1 with the highest power density achieved being 15.17 W·g −1 and energy density of 5.06×10 –4 Wh·g −1 . In addition, five 1D FSCs were hand-stitched and connected in series onto a cotton fabric. These supercapacitors could power a temperature and humidity sensor for up to six minutes, demonstrating the practicality and versatility of the prepared 1D FSCs for powering future electronic systems.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology