Simultaneous catalytic reduction of SO₂ and NO from flue gas using H₂S as a reductant at low temperatures

Xianghong Lu,Hao Li,Xiaohui Du,Xue Wang,Minyi Lan,Jianlin Wu,Jin Zhu,Jianliang Sun,Feng Jiang

DOI: https://doi.org/10.1039/c9re00347a

IF: 5.2002

2020-01-01

Reaction Chemistry & Engineering

Abstract:Although harmful NO and SO2 in flue gas can be separately removed by established technologies, such as selective catalytic reduction (SCR) or selective non-catalytic reduction (SNCR) and a wet scrubbing process, an integrated method for simultaneous desulfurization and denitrification is still in demand and attractive to improve energy efficiency and reduce investment and operation costs. Upon this, a novel sulfur-cycling integrated technology (simultaneous catalytic desulfurization and denitrification with H2S (H2S-SCDD)) has been proposed and is considered to be a profitable solution for the flue gas treatment. However, a high operation temperature (over 600 degrees C) is required in the H2S-SCDD process for the sulfur-cycling flue gas treatment as reported. To realize the H2S-SCDD process at low temperatures, different catalysts were prepared and tested, such as Al2O3-TiO2 (AT) loaded with transition metal oxides. The results show that a CeO2-loaded AT catalyst (Ce-AT) was the suitable catalyst to balance NO and SO2 removal by the H2S-SCDD process in the temperature range of 300-400 degrees C. Increasing Ce loading on AT significantly increased the NO conversion but had a slightly negative effect on SO2 reduction. With 15% Ce loading on the AT catalyst (Ce15-AT), the optimal temperature for the H2S-SCDD process was 240-280 degrees C. While at 280 degrees C, the SO2 and NO conversions were about 75% and 90%, respectively, implying the efficient and simultaneous reduction of NO and SO2. Upon this, the sulfur-cycling process is promising and attractive for flue gas treatment in industrial sectors.