Abstract:The sole micropores strictly restrict the wide utilization of TS-1 zeolite in the catalytic fields, especially in the catalytic conversion of compounds with large molecular sizes. Here, we report a feasible and economical method to overcome this drawback. In this work, the hierarchical TS-1 zeolite was constructed via post-acid treatment, post-alkali etching, and a combination of post-acid treatment and alkali etching methods, after which, the corresponding NiMo-supported catalysts were prepared via the incipient wetness impregnation method. Then, the aforementioned materials were fully characterized using X-ray diffraction (XRD), N-2 adsorption-desorption, pyridine adsorbed Fourier transform infrared spectroscopy (Py - FTIR), H-2 temperature programmed reduction (H-2 - TPR), X-ray photoelectron spectroscopy (XPS), and high-resolution transition electron microscope (HR-TEM) to unravel the changes in the physicochemical properties caused by the post treatments. Finally, the hydrodesulfurization of dibenzothiophene (DBT) was used as a probe to assess the effects of the post-treatments on the catalytic performance of the hierarchical NiMo/TS-1 catalysts. The results showed that the MFI topology of TS-1 zeolite remained undamaged significantly and the serial hierarchical TS-1 zeolites exhibited higher specific surface areas and mesopore structures. Moreover, appropriate amounts of Bronsted acid sites were formed at the surface of the serial hierarchical TS-1 zeolites. The interaction between the active metals and the support materials was also modulated by the post-treatment of TS-1 zeolite, which resulted in better dispersion of Ni promoted MoS2 slabs with a higher proportion of NiMoS active phase, further leading to the enhanced catalytic activity and direct desulfurization pathway selectivity of the corresponding serial hierarchical NiMo/TS-1 catalysts. Among all the prepared catalysts, the catalytic activity was enhanced by approximately 1.2 times over catalyst NiMo/AT-TS-1 obtained by post-acid treatment compared to that over catalyst NiMo/TS-1 without treatment and on which the selectivity of the DDS pathway was 22% higher compared to that over catalyst NiMo/TS-1.

In-depth Understanding the Role of Seeds in the Synthesis of TS-1

Hierarchical TS-1 zeolite loaded with NiMo catalysts: Preparation and performance in hydrodesulfurization

Seed-assisted synthesis of SAPO-34 zeolites: Genetic effect of seeds

Enhanced Catalytic Oxidation by Hierarchically Structured TS-1 Zeolite

Seed-assisted synthesis of TS-1 crystals containing Al with high catalytic performances in cyclohexanone ammoximation

Synthesis of Titanium Silicalite-1 with Small Crystal Size by Using Mother Liquid of Titanium Silicalite-1 As Seed

Influences of Seeds on the Properties of Zeolite NaA Membranes on Alumina Hollow Fibers

Seed-induced synthesis of functional MFI zeolite materials: Method development, crystallization mechanisms, and catalytic properties

Tailoring Porosity and Titanium Species of TS-1 Zeolites via Organic Base-assisted Sequential Post-treatment

Seed-induced Synthesis of Functional MFI Zeolite Materials: Method, Mechanism, and Catalytic Property

Seed-assisted synthesis of a nanosheet-assembled hierarchical SSZ-13 zeolite by coupling a small amount of TMAdaOH with TPOAC

STUDIES ON THE PROCESS OF Ti INCORPORATION INTO THE FRAMEWORK DURING THE CRYSTALLIZATION OF TS-1 ZEOLITE

The Ultrasound-Assisted Preparation of Crystal Seeds for the Hydrolysis of TiOSO4 to H2TiO3

Tetrapropylammonium Hydroxide Treatment of Aged Dry Gel to Make Hierarchical TS-1 Zeolites for Catalysis

Synthesis of High-Performanced Titanium Silicalite-1 Zeolite at Very Low Usage of Tetrapropyl Ammonium Hydroxide

Tailor-Made Nanoseeds for the Synthesis of Zeolites with Nanosized Dimensions

Insights on Seed Selection Criteria of SAPO-34 Synthesis: Structure Units and Chemical Microenvironment

Seed-induced, structure directing agent-free crystallization of sub-micrometer zeolite ZSM-5: A population balance analysis

Studies on the crystallization process of titanium silicalite-1 (TS-1) synthesized using tetrapropylammonium bromide as a template

Synthesis of TS-1 Molecular Sieve Membrane and Specification

SYNTHESIS OF TS-1 ZEOLITE Ⅰ. 29Si and 1H High-Resolution NMR Investigation on the Hydrolysis of Tetraethyl Orthosilicate