Abstract:Cold-rolling Fe22Co22Ni20Cr22Mn14 high entropy alloy (with a deformation of 70%), and annealing it at two temperatures (1100 and 800 °C) respectively created a bimodal grain size distribution in large-grain (LG) samples having an average grain size of 45.9 ± 20.0 μm and in small-grain (SG) samples having an average grain size of 4.3 ± 3.0 μm. Under three cryogenic temperatures (−50, −100, and −150 °C), high-speed deformation (~9 × 103 s−1) was conducted on a split Hopkinson pressure bar (SHPB) system to investigate the microstructural evolution of deformation nanotwins in the bimodal-structured samples. Subjected to high-speed deformation at decreasing cryogenic temperatures, the mechanical behaviors of LG samples were superior to those of SG samples. Notably, under high-speed deformation at −150 °C, LG structures achieved excellent mechanical strength of ~3.3 GPa with good ductility of ~31.9%. Profuse lamellar annealing nanotwins, which pre-existed in the coarse grains of LG samples, promoted efficient refinement strengthening. High-resolution transmission electron microscopy (HR-TEM) clearly revealed that the deformation nanotwins induced by high-speed deformation further refined the pre-existing annealing nanotwins in the coarse grains of LG samples, presumably providing advanced mechanical sustainability for high-speed deformation at cryogenic temperatures. It is suggested that the micrometer-scaled and nanometer-scaled annealing twins appear first in the matrices of coarse grains, enhancing the initial work-hardening; subsequently the deformation nanotwins form in pre-existing annealing nanotwins and narrow strips of the matrix, effectively providing the dynamic grain refinement and the work hardening capacity.

Deformation Nanotwins Suppress Shear Banding During Impact Test of CrCoNi Medium-Entropy Alloy

Atomistic and Theoretical Insights on Nanoprecipitates-Controlled Strengthening Behavior for Optimum Mechanical Performance in Nanotwinned NiCoCr Alloys

A Molecular Dynamics Study on Mechanical Performance and Deformation Mechanisms in Nanotwinned NiCo-based Alloys with Nano-Precipitates under High Temperatures

Bending-induced Deformation Twinning in Body-Centered Cubic Tungsten Nanowires

Discrete Twinning Dynamics and Size-Dependent Dislocation-to Twin Transition in Body-Centred Cubic Tungsten

Twinning and stacking fault formation during tensile deformation of nanocrystalline Ni

Deformation Twinning Mechanisms in Nanocrystalline Ni

Multiple deformation mechanisms induced by pre-twinning in CoCrFeNi high entropy alloy

Deformation nanotwins in coarse-grained aluminum alloy at ambient temperature and low strain rate

Atomic-Scale In Situ Observations of Reversible Phase Transformation Assisted Twinning in a CrCoNi Medium-Entropy Alloy

Anisotropic Mechanical Properties and Deformation Mechanisms of Nanotwinned Ni and Ni Alloys With Extremely Fine Twin Boundary Spacings

Plastic Deformation Behavior of Pre-Twinned CoCrFeNi High Entropy Alloy under Quasi-Static and Dynamic Deformation

Twinning-governed plastic deformation in a thin film of body-centred cubic nanocrystalline ternary alloys at low temperature

Curved Nanotwinned Structure in Ni Induced by Dynamic Compression

Investigation of nanotwins in the bimodal-structured Fe22Co22Ni20Cr22Mn14 alloy subjected to high-strain-rate deformation at cryogenic temperatures

Effects of nanotwins and stacking faults on the mechanical properties of CrCoNi medium-entropy alloys

Twinning dominated microstructural evolution in tungsten under impact loading

Enhanced Strain Hardening Induced by Twin Boundary-Dislocation Interaction in Micro-Pillar Compression of CoCrNi Medium-Entropy Alloy

Origin of the High Propensity for Nanoscale Deformation Twins in CrCoNi Medium-Entropy Alloy

High Impact Toughness of CrCoNi Medium-Entropy Alloy at Liquid-Helium Temperature

Plastic deformation mechanism of CoCrxNi medium entropy alloys