Abstract:Medium- and high-entropy alloys based on the CrCoNi-system have been shown to display outstanding strength, tensile ductility and fracture toughness (damage-tolerance properties), especially at cryogenic temperatures. Here we examine the JIc and (back-calculated) KJIc fracture toughness values of the face-centered cubic, equiatomic CrCoNi and CrMnFeCoNi alloys at 20 K. At flow stress values of ~1.5 GPa, crack-initiation KJIc toughnesses were found to be exceptionally high, respectively 235 and 415 MPa(square-root)m for CrMnFeCoNi and CrCoNi, with the latter displaying a crack-growth toughness Kss exceeding 540 MPa(square-root)m after 2.25 mm of stable cracking, which to our knowledge is the highest such value ever reported. Characterization of the crack-tip regions in CrCoNi by scanning electron and transmission electron microscopy reveal deformation structures at 20 K that are quite distinct from those at higher temperatures and involve heterogeneous nucleation, but restricted growth, of stacking faults and fine nano-twins, together with transformation to the hexagonal closed-packed phase. The coherent interfaces of these features can promote both the arrest and transmission of dislocations to generate respectively strength and ductility which strongly contributes to sustained strain hardening. Indeed, we believe that these nominally single-phase, concentrated solid-solution alloys develop their fracture resistance through a progressive synergy of deformation mechanisms, including dislocation glide, stacking-fault formation, nano-twinning and eventually in situ phase transformation, all of which serve to extend continuous strain hardening which simultaneously elevates strength and ductility (by delaying plastic instability), leading to truly exceptional resistance to fracture.

High Impact Toughness of CrCoNi Medium-Entropy Alloy at Liquid-Helium Temperature

Exceptional damage-tolerance of a medium-entropy alloy CrCoNi at cryogenic temperatures

Exceptional fracture toughness of CrCoNi-based medium- and high-entropy alloys close to liquid helium temperatures

Exceptional fracture toughness of CrCoNi-based medium- and high-entropy alloys at 20 kelvin

Dynamically Compressive Behaviors and Plastic Mechanisms of a CrCoNi Medium Entropy Alloy at Various Temperatures

Unveiling the Stacking Fault-Driven Phase Transition Delaying Cryogenic Fracture in Fe-Co-Cr-Ni-Mo-C-Based Medium-Entropy Alloy

Excellent ductility and serration feature of metastable CoCrFeNi high-entropy alloy at extremely low temperatures

Dynamic impact behavior and deformation mechanisms of Cr(26)Mn(20)Fe20Co(20)Ni(14) high-entropy alloy

Outstanding Tensile Properties of a Precipitation-Strengthened FeCoNiCrTi0.2 High-Entropy Alloy at Room and Cryogenic Temperatures

Probing Deformation Mechanisms of a FeCoCrNi High-Entropy Alloy at 293 and 77 K Using in Situ Neutron Diffraction

Exceptional high-strain-rate tensile mechanical properties in a CrCoNi medium-entropy alloy

Unraveling the Deformation Behavior of the Fe45Co25Ni10V20 High Entropy Alloy

Real-time Nanoscale Observation of Deformation Mechanisms in CrCoNi-based Medium- to High-Entropy Alloys at Cryogenic Temperatures

Martensitic transformation in CrCoNi medium-entropy alloy at cryogenic temperature

Dynamic mechanical responses of the Al<sub>0.1</sub>CoCrFeNi high entropy alloy at cryogenic temperature

Tensile Properties of a Non-Equiatomic Ni–Co–V Medium Entropy Alloy at Cryogenic Temperature

Dynamic mechanical responses of the Al0·1CoCrFeNi high entropy alloy at cryogenic temperature

Contribution of coherent precipitates on mechanical properties of CoCrFeNiTi 0.2 high-entropy alloy at room and cryogenic temperatures

Superior Strength-Ductility Synergy and Strain Hardenability of Al/Ta Co-Doped NiCoCr Twinned Medium Entropy Alloy for Cryogenic Applications

Remarkable Strength of a Non-Equiatomic Co29Cr29Fe29Ni12.5W0.5 High-Entropy Alloy at Cryogenic Temperatures

Cryogenic Mechanical Behaviors of CrMnFeCoNi High-Entropy Alloy