Abstract:ZnO nanorods were grown on ITO substrates with different concentration of electrolyte by electrodeposition method. Microstructure, surface topography, photoluminescence Spectra, Raman spectra and water contact angle of the thin films were measured. The XRD results show all samples are hexagonal wurtzite and the intensity of diffraction peaks at (002) preferred orientation are strengthen as electrolyte concentration increase from 0.005 to 0.03 M. As the concentration increases, the average diameter, density and inclination of the ZnO nanorods increased. Room temperature photoluminescence spectras of the ZnO nanorods show a narrow UV band centering at about 377 nm and broad visible emissions around 600 nm and the UV peak intensity revealed a remarkable decreased. Raman spectras exhibit three peaks which are located at 439 cm(-1), 562 cm(-1) and 1095 cm(-1). All samples change from hydrophobicity to hydrophilic after one hour ultraviolet (UV) irradiation. (C) The Author(s) 2015. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution Non-Commercial No Derivatives 4.0 License (CC BY-NC-ND, http://creativecommons.org/licenses/by-nc-nd/4.0/), which permits non-commercial reuse, distribution, and reproduction in any medium, provided the original work is not changed in any way and is properly cited. For permission for commercial reuse, please email: oa@electrochem.org. All rights reserved.

Morphology controlled deposition of ZnO single micro-nanorods

Effects of Electrodeposition Electrolyte Concentration on Microstructure, Optical Properties and Wettability of ZnO Nanorods

Preparation and characterization of bat-like ZnO micro- and nanorods by adjusting oxygen flux

Controlled Crystal Growth of ZnO Nanobelts by Chemical Vapor Deposition Method

Shape controllable synthesis of ZnO nanorod arrays via vapor phase growth

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Morphological control of ZnO nanostructures by electrodeposition.

Nanostructured ZnO: from Monodisperse Nanoparticles to Nanorods

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Evolution of Zinc Oxide Nanostructures Through Kinetics Control.

Growth mechanism and diameter control of well-aligned small-diameter ZnO nanowire arrays synthesized by a catalyst-free thermal evaporation method.

Controllable Morphology of ZnO Nanostructures Via a Solvothermal Route

Growth and Properties of Nano ZnO

Synthesis of Branched Zno Nanorods on Various Substrates Via A Wet-Chemistry Route

Nano/Micro-Structured ZnO Rods Synthesized by Thermal Chemical Vapor Deposition with Perpendicular Configuration

Microcosmic Growth Process of ZnO Microrods

Morphology, Structure, and Optical Properties of ZnO nanorods/Eosin-y Grown via Microwave-assisted Hydrothermal Method

Eutectic Condensation and Nucleation in Vapor-Liquid-Solid Grown Zno Nanorod Arrays on Si Substrate

Zinc Oxide Nanostructures: Morphology Derivation and Evolution

Morphology Controlling and Optical Property of ZnO Prepared by Hydrothermal Method

Surface-depletion Controlled Gas Sensing of ZnO Nanorods Grown at Room Temperature