Abstract:Ni coatings with high catalytic efficiency were synthesised in this work, obtained by increasing the active surface and modifying Pd as a noble metal. Porous Ni foam electrodes were obtained by electrodeposition of Al on a nickel substrate. Deposition of Al was carried out with potential -1.9 V for a time of 60 min in NaCl-KCl-3.5 mol%AlF3 molten salt mixture at 900 °C, which is connected with the formation of the Al-Ni phase in the solid state. Dissolution of Al and Al-Ni phases was performed by application of the potential -0.5 V, which provided the porous layer formation. The obtained porous material was compared to flat Ni plates in terms of electrocatalytic properties for ethanol oxidation in alkaline solutions. Cyclic voltammetry measurements in the non-Faradaic region revealed the improvement in morphology development for Ni foams, with an active surface area 5.5-times more developed than flat Ni electrodes. The catalytic activity was improved by the galvanic displacement process of Pd(II) ions from dilute chloride solutions (1 mM) at different times. In cyclic voltammetry scans, the highest catalytic activity was registered for porous Ni/Pd decorated at 60 min, where the maximum oxidation peak for 1 M ethanol achieved +393 mA cm-2 compared to the porous unmodified Ni electrode at +152 mA cm-2 and flat Ni at +55 mA cm-2. Chronoamperometric measurements in ethanol oxidation showed that porous electrodes were characterised by higher catalytic activity than flat electrodes. In addition, applying a thin layer of precious metal on the surface of nickel increased the recorded anode current density associated with the electrochemical oxidation process. The highest activity was recorded for porous coatings after modification in a solution containing palladium ions, obtaining a current density value of about 55 mA cm-2, and for a flat unmodified electrode, only 5 mA cm-2 after 1800 s.

Electrocatalytic Oxidation of Ethanol and Ethylene Glycol on Bimetallic Ni and Ti Nanoparticle-Modified Indium Tin Oxide Electrode in Alkaline Solution

Nanoscale Ni-B electrocatalyst prepared from nickel ethylenediamine complex for direct ethanol electrocatalytic oxidation.

Ethanol oxidation on a nichrome-supported spherical platinum microparticle electrocatalyst prepared by electrodeposition

Pt Nanoparticles Supported Inside Tio2 Nanotubes for Effective Ethanol Electrooxidation

Pt Nanoparticles Dispersed on Ni/C Nanoflowers As Stable Electrocatalysts for Methanol Oxidation and Oxygen Reduction

Enhanced Catalytic Activities of NiPt Truncated Octahedral Nanoparticles Toward Ethylene Glycol Oxidation and Oxygen Reduction in Alkaline Electrolyte.

Pd Nanoparticles Supported on Tio2 Nanotubes for Ethanol Oxidation in Alkaline Media

FACILE SYNTHESIS OF Pt-/Pd-MODIFIED NiTi ELECTRODE WITH SUPERIOR ELECTRO-CATALYTIC ACTIVITIES TOWARD METHANOL, ETHANOL AND ETHYLENE GLYCOL OXIDATION

Preparation of Metallic Ni3N Nanoparticles and Its Electrooxidation Performance for Ethylene Glycol

NiO-induced Synthesis of PdNi Bimetallic Hollow Nanocrystals with Enhanced Electrocatalytic Activities Toward Ethanol and Formic Acid Oxidation

A New Kind of Highly Active Hollow Flower-Like NiPdPt Nanoparticles Supported by Multiwalled-Carbon Nanotubes Toward Ethanol Electrooxidation

Preparation of Well-Distributed Pt–Ni Nanoparticles On/into TiO2NTs by Pulse Electrodeposition for Methanol Photoelectro-Oxidation

Nano-structured PdxPt1−x/Ti Anodes Prepared by Electrodeposition for Alcohol Electrooxidation

Preparation Of Ni-Ti-O Nanotube Arrays Supported Nano-Ni(Oh)(2) Electrode And Its Electrocatalytic Oxidation Of Methanol

Pt Nanoparticles Supported on Submicrometer-Sized TiO2 Spheres for Effective Methanol and Ethanol Oxidation

Direct growth of NiCo2O4 nanostructures on conductive substrates with enhanced electrocatalytic activity and stability for methanol oxidation

PdNi/Ni Nanotubes Assembled by Mesoporous Nanoparticles for Efficient Alkaline Ethanol Oxidation Reaction.

Electrocatalytic Performance of Ni-Ti-O Nanotube Arrays/Niti Alloy Electrode Annealed under H-2 Atmosphere for Electro-Oxidation of Methanol

Electrocatalytic Performance of Ethanol Oxidation on Ni and Ni/Pd Surface-Decorated Porous Structures Obtained by Molten Salts Deposition/Dissolution of Al-Ni Alloys

From Bimetallic PdCu Nanowires to Ternary PdCu-SnO2 Nanowires: Interface Control for Efficient Ethanol Electrooxidation

Ni-Pt-Pd ternary alloy nanoparticles supported on carboxyl-modified carbon nanotubes as highly efficient catalyst for methanol and ethanol electrooxidation