A beehive-shaped Pd and Ni Nanoparticle Composite Showing Significant Electrocatalytic Activity Towards Ethanol Oxidation Reaction (EOR)
Keqiang Ding,Fujuan Shi,Dongyue Zhang,Boxia Li,Jiasheng Chen,Mengyao Di,Mengying Yan,Hui Wang,
DOI: https://doi.org/10.20964/2022.04.34
IF: 1.541
2022-04-01
International Journal of Electrochemical Science
Abstract:For the first time, a beehive-shaped palladium and nickel (PdxNiy) nanoparticle composite electrocatalyst for ethanol oxidation reaction (EOR) was prepared via a pyrolysis method using palladium oxide and the calcined product of a nickel acetylacetonate (NAA) as the starting materials. Firstly, a proper amount of NAA was respectively calcined at 300 ºC, 500 ºC and 700 ºC for 2 h in an air atmosphere producing three nickel-containing precursors, successively being employed to prepare the final sample of catalyst c1, c2 and c3. As displayed by the SEM images, c1, c2 and c3, respectively, delivered a rock-shaped, beehive-shaped and scorched earth-shaped morphology. As revealed by the TEM images, all resultant catalysts were accumulated by a large number of nanoparticles. XRD and XPS results strongly indicated that metallic Pd, PdO, NiO, metallic Ni and carbon materials were the main components of all as-prepared catalysts. More than that, as verified by the CV test, compared to other two catalysts, c2 exhibited a significant electrocatalytic activity towards EOR, that is, the EOR current density of the forward peak (25 mA cm-2) measured on c2 at 50 mV s-1, was almost 28 times higher than that of EOR on c3 (0.9 mA cm-2). Especially, the Faraday current density of EOR on c2 at 600 s, as demonstrated by the CA measurement, was as large as 16.5 mA cm-2, remarkably higher than that of EOR recorded on c1 (4.2 mA cm-2) and c3 (0.15 mA cm-2). Developing a novel kind of nickel-containing precursor and preparing a beehive-shaped high performance PdxNiy electrocatalyst for EOR were the main dedications of this preliminary work, which was very beneficial to the further exploration of Pd-based electrocatalysts.