Evolution of Microstructure and Nanohardness of SiC Fiber-Reinforced SiC Matrix Composites under Au Ion Irradiation

Chao Ye,Jiaxiang Xue,Tong Liu,Rui Shu,Yan,Yehong Liao,Qisen Ren,Guang Ran,Kai Sun,Li Jiang,Pengyuan Xiu,Lumin Wang
DOI: https://doi.org/10.1016/j.ceramint.2019.12.044
IF: 5.532
2020-01-01
Ceramics International
Abstract:Evolution of microstructure and nanohardness of a new type of SiCf/SiC composite under a 6 MeV Au ion irradiation up to 90 displacements per atom at 400 degrees C was studied. Scanning transmission electron microscopy reveals that the irradiation has induced enrichment of carbon at the grain boundaries in the fibers. This is attributed to the accumulation of C interstitials generated by the irradiation. The disappearance of {200} diffraction ring of 3C-SiC indicates that a phase transition from 3C-SiC to Si has occurred during irradiation. In addition, the hardness of SiC fiber increased after irradiation, which is due to the pinning effect caused by irradiation-induced defects. The pyrolytic-carbon interphase that contains Si-rich nano-grains in the composite has the highest irradiation tolerance as it maintained its basic morphology and graphitic nature after a radiation damage dose up to 90 dpa. Twins are the main internal defects in the SiC matrix of the SiCf/SiC composite, which grew up and resulted in the decrease of the number of twinning boundaries under irradiation. No significant microstructure change has been observed in the SiC matrix except a limited number of dislocation loops at the peak irradiation damage region. The entire matrix still maintained its hardness after irradiation.
What problem does this paper attempt to address?