Enhanced Osteogenic Differentiation of Osteoblasts on CaTiO3 Nanotube Film.

Yanni Zhang,Kun Wang,Kai Dong,Ning Cui,Tingli Lu,Yong Han

DOI: https://doi.org/10.1016/j.colsurfb.2020.110773

IF: 5.999

2020-01-01

Colloids and Surfaces B Biointerfaces

Abstract:Improved implant-bone interface interaction for rapid formation of strong and long-lasting bond is significantly important in orthopedic clinics. Herein, Ca-doped TiO2 nanotube film (M-CaNTs) with enhanced adhesion strength was fabricated on titanium (Ti) surface by an anodization-hydrothermal treatment. Results showed that TiO2 nanotube film (M-NTs) fabricated by modified anodization was amorphous, exhibiting 100-nm diameter and 12-nm tube wall thickness. After hydrothermal treatment, the nanotubular structure of M-CaNTs kept integrated, but was volume-expanded, exhibiting a decreased diameter (similar to 60 nm) and an increased wall thickness (similar to 30 nm). The formation of M-CaNTs proceeded preferentially at the interior surfaces of the closely aligned nanotubes, involving an in situ dissolution-recrystallization process. Though the adhesion strength of M-CaNTs was weakened by the volume-expansion derived internal stress, it was still higher than that of the traditionally obtained one. In the in vitro investigations, the combination of nanotubular structure and Ca2+ could expectedly enhance the attachment, spreading and proliferation of MC3T3-E1 cells, as well as promote the expressions of bone-specific genes, intracellular proteins and ALP activity, which in turn accelerated collagen secretion and ECM mineralization. This work provides an attractive potential for the surface modification of Ti-based implants in clinical application.