Abstract:Obtaining a reliable NiTi–Ti6Al4V(TC4) heterogeneous alloy component exhibiting excellent strength and elasticity via integrating distinct material benefits can provide design flexibility in multifunctional device fabrication. However, the fabrication of this materials couple is challenging due to the development of excessive Ti2Ni intermetallic compound. Inspired by the bioheterogeneous layered structure, Nb interlayer was applied for the wire arc additive manufacturing (WAAM) of NiTi and TC4 to restrict the mixing of alloying elements on both sides. However, the strength of NiTi–Nb-TC4 alloy component was limited by pure Nb characteristics when the NiTi and TC4 was completely separated by the unmolten Nb interlayer. In this work, the tensile strength perpendicular to the interface of NiTi–Nb-TC4 alloy component was enhanced to introduce appropriate amount Ni and Ti in Nb interlayer by adjusting the composite WAAM process at the expense of Ti2Ni. Microstructure evolution, composition change and mechanical properties of composite WAAM NiTi–Nb-TC4 alloy component were investigated. It was shown that the compression strength and fracture strain perpendicular to the interface of WAAM NiTi–Nb-TC4 sample was 1549.0 ± 17 MPa and 22.3 ± 8 %, and the compressive strength can reach 63.6 % and 94.5 % of WAAM NiTi alloy and TC4 alloy, respectively. The composite WAAM NiTi–Nb-TC4 sample maintained 65.3 % recovery rate after ten compression cycles, which confirmed that partial superelasticity was maintained in the WAAM NiTi–Nb-TC4 multilayer structure. This fact further proved that WAAM can be successfully applied to deposit shape memory/superelastic alloys. The use of the Nb interlayer enhanced the tensile strength perpendicular to the interface to 460.7 ± 16 MPa. The ultimate tensile strength perpendicular to the interface of composite WAAM NiTi–Nb-TC4 sample can reach 72.0 % and 60.0 % of WAAM NiTi alloy and TC4 alloy, respectively. The formation of NiTi, TiNb and β-Nb phases in Nb interlayer and the network distribution of Ti2Ni and TiNb phases explained the improved mechanical performance of the composite WAAM NiTi–Nb-TC4 alloy component.

Microstructure and mechanical properties of the Nb37.7Mo14.5Ta12.6Ni28.16Cr7.04 multi-principal alloys fabricated by gas tungsten wire arc welding additive manufacturing

Microstructure and Mechanical Properties of Wire Arc Additively Manufactured MoNbTaWTi High Entropy Alloys

Microstructure and properties of a Ni–Ti–Cr–Mo–Nb alloy fabricated in situ by dual-wire arc additive manufacturing

Microstructure and mechanical properties of twin wire and arc additive manufactured Ni3Al-based alloy

Microstructure and Properties of a Novel Ni-Ti-Cr-Mo-Nb Alloy Fabricated in Situ by Dual-Wire Arc Additive Manufacturing

Microstructures and mechanical properties of NiTi shape memory alloys fabricated by wire arc additive manufacturing

Multi-material wire arc additive manufacturing of a bio-inspired heterogeneous layered NiTi/Nb/Ti6Al4V structure: Microstructural evolutions and mechanical properties

Microstructure and Mechanical Properties of NiCrMoV Steel Fabricated by Double-Electrode Gas Metal Arc Additive Manufacturing

Wire-based directed energy deposition of NiTiTa shape memory alloys: Microstructure, phase transformation, electrochemistry, X-ray visibility and mechanical properties

Microstructure and mechanical properties of TC4/NiTi bionic gradient heterogeneous alloy prepared by multi-wire arc additive manufacturing

In-situ fabrication of Ti<sub>2</sub>AlNb-based alloy through double-wire arc additive manufacturing

Microstructural evolution and mechanical properties of Ni-based superalloy joints brazed using a ternary Ni-W-B amorphous brazing filler metal

Precipitation characteristics and tensile properties of high-nitrogen chromium-manganese steel fabricated by wire and arc additive manufacturing with isothermal post-heat treatment

Phase constitution, microstructure and mechanical properties of a Ni-based superalloy specially designed for additive manufacturing

In-situ synthesis of Alx-Co-Cr-Ni high entropy alloys via twin-wire and arc additive manufacturing (T-WAAM): microstructure evolution and mechanical properties

Wire and arc additive manufacturing of a Ni-rich NiTi shape memory alloy: Microstructure and mechanical properties

Microstructure evolution and mechanical properties of Al–Cu–Mn–Cd alloy fabricated by CMT-wire arc additive manufacturing

Microstructure and mechanical properties of dual wire-arc additive manufactured Al-Co-Cr-Fe-Ni high entropy alloy

Research on Technology of 7075 Aluminum Alloy Processed by Variable Polarity TIG Additive Manufacturing Utilizing Nanoparticle-Reinforced Welding Wire with TiB2

Influence of Interlayer Temperature on Microstructure and Mechanical Properties of Additively Manufactured Inconel 625

L1 2 nanoparticle-strengthened CoNi-based superalloy with ultrahigh yield stress developed using CALPHAD method