Revealing microstructural evolutions, mechanical properties and wear performance of wire arc additive manufacturing homogeneous and heterogeneous NiTi alloy
J.Z. Teng,P.F. Jiang,X.H. Cui,M.H. Nie,X.R. Li,C.Z. Liu,Z.H. Zhang
DOI: https://doi.org/10.1016/j.jmrt.2023.10.055
IF: 6.267
2023-10-12
Journal of Materials Research and Technology
Abstract:Heterogeneous microstructure designs have attracted a great deal of attention, not only because they have the potential to achieve an ideal combination of two conflicting properties, but also because the processes involved in their fabrication are cost-effective and can be scaled up for industrial production. The process parameters in the preparation process have an important effect on the microstructure and properties of alloy members prepared by wire arc additive manufacturing (WAAM) technology. It was expected that the spatial heterogeneous microstructure with large microstructural heterogeneities in metals can be formed through changing the process parameters. In this work, homogeneous NiTi thin-walled component and heterogeneous NiTi thin-walled component were fabricated using WAAM technology by adjusting the heat input. The effects of deposition height and heat input on the microstructure, mechanical properties and wear properties of WAAM NiTi alloys were investigated. The results show that grains were gradually refined with the increase of deposition height in the homogeneous WAAM NiTi component. The ultimate tensile strength of homogeneous WAAM NiTi component increased from 606.87 MPa to 654.45 MPa and the elongation increased from 12.72% to 15.38%, as the increase of deposition height. Moreover, the homogeneous WAAM NiTi component exhibited excellent wear resistance, the coefficient of friction decreased from 0.760 to 0.715 with the increase of deposition height. Meanwhile, the grains in the heterogeneous WAAM NiTi component shows the finest grains in the central region. The ultimate tensile strength of the lower region, middle region and upper region of heterogeneous WAAM NiTi components were 556.12MPa, 599.53MPa and 739.79MPa, and the elongations were 12.98%, 16.69%, 21.74%, respectively. The coefficient of friction for the lower region, middle region and upper region of heterogeneous WAAM NiTi components were 0.713, 0.720 and 0.715, respectively. The microhardness and cyclic compression properties of the homogeneous components with higher heat input were better than those of the heterogeneous components for the same deposition height. The tensile yield strength, elongation and wear resistance of the heterogeneous components were superior compared to the homogeneous components. These results can be used to optimize the WAAM process parameters to prepare NiTi components with excellent mechanical properties.
materials science, multidisciplinary,metallurgy & metallurgical engineering