Abstract:Ti44Al6Nb1.0Cr2.0V alloy was directionally solidified (DS) with cold crucible under different input powers (40 kW, 45 kW, 48 kW and 50 kW; corresponding to temperature gradient of 15.2 K/mm, 21.0 K/mm, 22.9 K/mm, 25.5 K/mm) and the same pulling velocity (8.33 mu m/s). The results show that all the DS samples have the beta-solidification characteristics and when the power is 45 kW or 48 kW, they have the well-DS macrostructure. After DS, the lamellar width becomes smaller and more homogeneous from the as-cast 1650 +/- 1200 nm to less than 710 +/- 376 nm. The higher the power is, the smaller the lamellar width it has. The original casting microcracks can be eliminated after DS and the percentage of small angle lamellas is higher for the well-DS samples. For the DS samples, the nanoindentation hardness in lamella region and the lamellar width yield the relationships of H-N = 16.12d(-0.127) and r(2) = 0.992. When the as-cast and heat treatment (HT) conditions are considered, the relationships are changed as H'(N) = 16.09d'(-0.127) and r'(2) = 0.971. The nanoindentation hardness of B-2 phase and block gamma phase keep almost the same respectively under the different conditions. RT tensile property is improved to average UTS 589.4 MPa and average elongation 1.16% after DS (P = 45 kW) comparing with the original as-cast 498.8 MPa and 0.53%. Trans-granular and trans-lamella fracture is the main fracture mode for the DS samples. After annealing (at 1250 degrees C, 1300 degrees C, 1350 degrees C), lamellar width is coarsen to more than 2002 +/- 1286 nm; B-2 phase segregation is reduced obviously, but some new microcracks form; HT samples exhibits a poor RT tensile property, in which the HT2 sample has a relatively higher property and it yields the average UTS 440.6 MPa and average elongation 0.45%. (C) 2015 Elsevier B.V. All rights reserved.

Microstructure Evolution of Ti44Al Alloy During Directional Induction Heat Treatment and Its Effect on Mechanical Properties

Optimizing microstructure and mechanical properties of directionally solidified Ti44Al6Nb1Cr2V alloy by directional heat treatment

Study on improving directional microstructure of Ti44Al6Nb1Cr alloy by continuous regional phase transformation

Microstructure Evolution and Mechanical Properties of Directionally-Solidified TiAlNb Alloy in Different Temperature Gradients

Effect of Cyclic Heat Treatment on Microstructures and Mechanical Properties of Directionally Solidified Ti–46Al–6Nb Alloy

Effect of Heat Treatment on Microstructures and Mechanical Properties of a Novel Β-Solidifying TiAl Alloy

Effect of Heat Treatment on Microstructure and Mechanical Properties of Cast and Directionally Solidified High-Nb Contained TiAl-based Alloys

A novel method to prepare columnar grains of TiAl alloys by controlling induction heating

Effects of Heating Power on Microstructure Evolution and Tensile Properties at Elevated Temperature by Directional Solidification for Ti2AlC/TiAl Composites

Effects of Thermo-Mechanical Treatment on Microstructure and Mechanical Property of Ti-45al-5nb-0.3y Alloy

Effects of heat treatment on the microstructures and mechanical properties of as-cast Ti-45Al-2Nb-2Cr-(0.2, 0.5) C alloys

Effect of Heat Treatment on the Microstructure and Mechanical Properties of TiAl Alloys

Microstructural Control and Mechanical Properties of Ti–47Al–2Cr–2Nb Alloy by Directional Solidification Electromagnetic Cold Crucible Technique

The Growth Behavior of Columnar Grains in a TiAl Alloy During Directional Induction Heat Treatments

EFFECTS OF THERMO-MECHANICAL TREATMENTS ON MICROSTRUCTURE OF Ti-43Al-9V-Y ALLOY

The Effect of Heat Treatment on the Microstructure and Mechanical Properties of Powder Metallurgy Ti-48Al Alloy

Effects of cycle heat treatment on the microstructure and mechanical property of as-cast ?-TiAl alloy

The Effect of Heat Treatment on the Microstructure of Ti-45Al-5Nb-0.3Y Alloy

Microstructural Evolution and Mechanical Properties of Forged Β-Solidified Γ-Tial Alloy by Different Heat Treatments

Effect of Heat Treatment on the Microstructure and Tensile Properties of Deformed Α/β Ti–47Zr–5Al–3V Alloy

Investigation of α phase evolution and tensile fracture behavior of Ti5Al2Sn2Zr4Mo4Cr alloy fabricated by directed energy deposition