PREPARATION AND OSTEOBLAST AFFINITY OF BOVINE HYDROXYAPATITE
高媛,孔丽君,王晨,公衍道,田杰谟,赵南明,张秀芳
DOI: https://doi.org/10.3321/j.issn:1000-6737.2004.06.011
2004-01-01
ACTA BIOPHYSICA SINICA
Abstract:Hydroxyapatite derived from nature bone has the characteristics of good biocompatibilities, suitable surface chemistry and three dimension porous-network systems. Two groups of porous hydroxyapatite ceramics, sample 1 and sample 2, were prepared by sintering of bovine bone at 1 120 and 1 250℃, respectively. They were characterized by scanning electron microscopy (SEM), mercury intrusion porosimetry, wide angle X-ray diffraction (XRD) and fourier transform infrared spectroscopy (FT-IR). Further, MTT assay was used to investigate the proliferation of mouse preosteoblastic cells cultured on the hydroxyapatite scaffolds, and the activity of alkaline phosphatase (ALP), a marker for osteoblast differentiation, was quantitatively detected. The cells attachment on the materials were observed by SEM.The porous materials of high purity consisted of a unique normal hydroxyapatite structure was confirmed by XRD and FT-IR measurements. When cells were cultured on the hydroxyapatite scaffolds, 1.0 cm × 1.0 cm × 0.2 cm size, no proliferation inhibition was found. Osteoblasts proliferation was significantly greater on sample 1 than on sample 2 after 1, 3, 7 and 10 days of culture. There was significant difference on ALP activity of osteoblasts cultured on sample 1 in comparison with sample 2 after 7, 14, 21 and 28 days. Compared to sample 2, sample 1 turned to be excellent scaffold materials. These results suggest that bovine hydroxyapatite is a promising material for bone repairing and provide further basis for the use of natural bones as the scaffold in bone tissue engineering.