A Simple Co-Impregnation Route to Load Highly Dispersed Fe(III) Centers into the Pore Structure of SBA-15 and the Extraordinarily High Catalytic Performance
Yongsheng Li,Yong Chen,Liang Li,Jinlou Gu,Wenru Zhao,Lei Li,Jianlin Shi
DOI: https://doi.org/10.1016/j.apcata.2009.06.028
IF: 5.723
2009-01-01
Applied Catalysis A General
Abstract:Highly dispersed iron centers supported on SBA-15 were successfully prepared via a simple incipient wetness co-impregnation route by casting furfuryl alcohol (FA) solution of iron (111) acetylacetonate (Fe(acac)(3)), which were used as carbon and iron sources, respectively, into the pore structure of SBA-15, followed by the subsequent removal of carbonized FA. Various techniques such as XRD, TEM, N-2 sorption, UV-vis, XPS and EPR, were employed to characterize the prepared catalysts. It was shown that both Fe2O3 nanoclusters and isolated iron species were present and highly dispersed onto the pore surface of SBA-15. due to the presence of abundant carbon source co-impregnated, with well-maintained, highly ordered and open mesoporous structure. A great number of acidities was introduced by the loading of Fe2O3, and the catalytic performance was tested on the Friedel-Crafts benzylation of benzene by benzyl chloride. Under the optimized reaction condition, the catalyst showed a superior catalytic performance with a 100% yield of monoalkylated product within 1.5 min at 60 degrees C. The catalyst demonstrated high reusability and stability, the yield of diphenyl methane was still higher than 90% after 6 runs. Moreover, the catalyst was still active at the temperatureas low as 40 degrees C. Such a strategy is verified applicable to prepare other well-dispersed metal oxides, i.e. MnxOy loaded into the pore structure of mesoporous materials. (C) 2009 Elsevier B.V. All rights reserved.