Abstract:A novel technique, for the fabrication of large size Yb3+ doped silica glass rod with a diameter of 3 mm and a length of 270 mm and thus a large-core double-clad fiber with a diameter of 80 p.m and an outer cladding layer diameter of 100 p.m by the glass phase-separation technology, is reported. The refractive index profile, Yb3+ absorption spectrum and background loss arc experimentally tested, and the laser performances arc also demonstrated. The results show that the refractive index distributes uniformly within the active fiber core of this fiber and the the numerical aperture is about 0.065. The doping concentration of Yb3+ (mass fraction) is 1.22%, the absorption coefficient at 976 nm is 6.5 dB/m, and the background loss at 793 nm is 0.03 dB/m. Based on the power amplifier structure of the master oscillator, the lasing output at 1080 nm is realized for this fiber when pumped by a diode laser at 976 nm, where the fiber length is 2.5 m, the slope efficiency is 78 0, and the maximum laser output power is 300 W. The glass phase-separation technique provides a novel technique route to fabricate the active silica glass core rods with large size and high uniformity, which has a high potential in the fabrication of heavily doped extra-large-core fibers and active fibers with a complex core structure.

Manufacture and Spectroscopic Analysis of Tm3+-doped Silica Glass and Microstructure Optical Fiber Through the Laser Sintering Technique

Tm/Al Co-Doped Silica Glass Prepared by Laser Additive Manufacturing Technology for 2-Μm Photonic Crystal Fiber Laser

Tm 3+ doped lead silicate glass single mode fibers for 2.0 μm laser applications

Tm^3+ Doped Lead Silicate Glass Single Mode Fibers for 20 Μm Laser Applications

1.8μm fluorescence characteristics of Tm3+ doped silica glasses and fiber prepared by the glass phase-separation technology

Tm 3+ doped barium gallo-germanate glass single-mode fibers for 2.0 μm laser

Development of High Efficiency Tm3+-doped Fiber and Tm3+-doped Fiber Laser

Tm³⁺ doped barium gallo-germanate glass single-mode fibers for 2.0 μm laser.

1887 Nm Lasing in Tm3+-doped TeO2-BaF2-Y2O3 Glass Microstructured Fibers

Highly Tm(3+) Doped Germanate Glass and Its Single Mode Fiber for 2.0 Μm Laser.

Extra-Large-Core Yb3+ Doped Fiber and Its Laser Research Based on Glass Phase-Separation Technique

Controllable structural tailoring for enhanced ∼2 µm emission in heavily Tm3+-doped germanate glasses.

Spectroscopic and Laser Properties of Al-P Co-Doped Yb Silica Fiber Core-Glass Rod and Large Mode Area Fiber Prepared by Sol-Gel Method

4.3 GHz fundamental repetition rate passively mode-locked fiber laser using a silicate-clad heavily Tm<sup>3+</sup>-doped germanate core multimaterial fiber

4.3 GHz fundamental repetition rate passively mode-locked fiber laser using a silicate-clad heavily Tm3+-doped germanate core multimaterial fiber

Tm 3+ -doped tellurium germanate glass and its double-cladding fiber for 2μm laser

3D Nanoporous Silica Rods for Extra-Large-Core High-Power Fiber Lasers

The Preparation of Yttrium Aluminosilicate (YAS) Glass Fiber with Heavy Doping of Tm3+ from Polycrystalline YAG Ceramics

Controllable Structural Tailoring for Enhanced ∼2 Μm Emission in Heavily Tm3+-doped Germanate Glasses

Single-Mode Large Mode-Field-Area Tm<sub>3+</sub>-Doped Lead-Silicate Glass Photonic Crystal Fibers

Enhanced CW Lasing and Q‐Switched Pulse Generation Enabled by Tm3+‐Doped Glass Ceramic Fibers