Abstract:Using electrochemical impedance spectroscopy (EIS) technique, the analyses of impedance models and the water uptake processes of epoxy-coated mild steels and LY12 aluminum alloys immersed in 3.5% (weight fraction) NaCl solution were studied. The fitting results using suitable electrical equivalent circuits (EEC) suggested that there were four kinds of impedance models in the course of immersion. In the initial period of immersion, an EEC containing the coating capacitance and the coating resistance was used to fit the EIS data. Along with the immersion time, the number of time-constant of impedance spectra for metal/coating systems increased, indicating that corrosion reaction took place. After a certain time's attacking of metal substrates, the diffusion process towards solution of corrosion products forming at the metal/coating interface might be restrained due to the presence of coating barrier, resulting in the appearance of diffusion elements. This diffusion did not act as an ideal Warburg behavior, leading to a deviation of dispersive number, n, from 0.5. After longer immersion times, the Cl− ions reached the surface of metal through the coating and participated in chemical reactions with corrosion products to form salt film on aluminum alloy surface. The formation of chloride ion-incorporation salt film resulted in the change of impedance spectrum characteristics. The studies revealed that the water transport in epoxy varnish coatings followed the Fickian diffusion law during the initial time of exposure to the testing solution. After immersion for a certain time, the water uptake reached saturation and the coating capacitance tended to a relatively steady value. According to the variation of coating capacitance with time, the water diffusion coefficient was deduced. The experimental results indicated that the water diffusion coefficients in epoxy coatings were slightly dependent on coating thickness and were to some extent influenced by substrate type. The similar surface chemical structures of epoxy coatings on different metals were found from the Fourier transform infrared spectroscopy (FT-IR)–attenuated total reflection (ATR) measurements. The glass transition temperature (Tg) of epoxy coatings prepared on different metal substrates before and after immersion was measured by using differential scanning calorimetry (DSC). Lower diffusion rate of water in Al alloy based epoxy films than that in steel based ones was interpreted by the higher absolute value and smaller decrease of Tg of organic coatings painted on the former substrate.

Evaluation of Coating Resistivity for Pigmented/unpigmented Epoxy Coatings under Marine Alternating Hydrostatic Pressure

Study of the Failure Mechanism of an Epoxy Coating System under High Hydrostatic Pressure

Evaluating the Diffusion Coefficient of Different Epoxy Resins with EIS

Investigating an Effective Model to Estimate the Water Diffusion Coefficient of a Hybrid Polymer-Oxide Coating

Electrochemical impedance spectroscopy of multi-layer epoxy coatings in NaCl solution

Study and Application of Electrochemical Impedance Spectroscopy for Quickly Evaluating the Performance of Coatings and Predicting the Failure Time in the Development of Waterborne Epoxy Micaceous Iron Oxide Coatings

Degradation Behavior of a Modified Epoxy Coating in Simulated Deep-sea Environment

Electrochemical Impedance Spectroscopy Study on the Diffusion Behavior of Water through Epoxy Coatings

Studies of Impedance Models and Water Transport Behaviors of Polypropylene Coated Metals in NaCl Solution

Corrosion Electrochemical Characteristics of Red Iron Oxide Pigmented Epoxy Coatings on Aluminum Alloys

Experiment and Model Validation of Water Concentration Jump of a Composite Coating on 2024 Al Alloy

EIS study of effective capacitance and water uptake behaviors of silicone-epoxy hybrid coatings on mild steel

Synergistic effects of fluid flow and hydrostatic pressure on the degradation of epoxy coating in the simulated deep-sea environment

Study on distributed resistivity and protective performance of silicone epoxy coatings with and without filler under tensile stress

Studies of water transport behavior and impedance models of epoxy-coated metals in NaCl solution by EIS

Effect of Pigment Volume Concentration on Properties of Waterborne Antistatic Anticorrosive Epoxy Coating

EIS INVESTIGATION FOR PERFORMANCE MECHANISM OF PIGMENT Pb_3O_4 IN ORGANIC COATING

Study on the Failure Behavior of Epoxy Coating in a Seawater Environment with Alternate Pressures Conditions

Eis Studies of Water Transport in Epoxy Coatings Coated on Ly12 Aluminum Alloys

Influence of AC-DC-AC Cycling with Hydrostatic Pressure on Accelerated Protective Performance Test of Glass Flake Epoxy Coating

EFFECT OF CYCLIC PRESSURE ON DEGRADATION BEHAVIOR OF EPOXY COATING IN SIMULATED DEEP OCEAN ENVIRONMENT