Popcorn-based Dual-Monomer Copolymerized Temperature/ph-Sensitive Core-Shell Hydrogels
Wenxu Zhang,Xuyang Mu,Yan Xu,Sijie Li,Xiaoming Liu,Ziqiang Lei
DOI: https://doi.org/10.1016/j.jece.2023.109510
IF: 7.7
2023-01-01
Journal of Environmental Chemical Engineering
Abstract:Temperature/pH-responsive hydrogels are one of the most studied environmental-responsive hydrogels, with sensitivity and rapid response being the sought-after properties, while sensitivity and reusability are generally poor. This study prepared a hydrogel with a temperature/pH-responsive core-shell structure by static template polymerization, using the temperature-sensitive monomer dimethylaminoethyl methacrylate polymerized with 2-acrylamide-2-methylpropanesulfonic acid as the temperature-sensitive shell and popcorn with acrylic acid as the pH-responsive core-layer hydrogel. The chemical structure, thermal stability, and morphology of the core -shell structure hydrogels were characterized by Infrared spectroscopy (FTIR), X-ray diffraction (XRD), Brunauer-Emmett-Teller surface (BET), Scanning electron microscopy (SEM), Atomic force microscopy (AFM) and Thermogravimetric analysis (TG), respectively. The pH responsiveness well as the temperature respon-siveness of the shell structure was tested. The results showed that the lowest critical solution temperature (LCST) of the core-shell hydrogel is 43 degrees C, with good temperature responsiveness in the range of 25-55 degrees C, pH responsiveness from pH= 4 to pH= 13, and a short response time. From SEM, AFM, and BET, it can be concluded that the hydrogel has a rough surface and pore structure with a root mean square roughness value of 0.787 nm, a specific surface area of 1.3381 m2/g, and an average pore size of 4.0911 nm. FTIR and XRD can show that popcorn (PCP) is well-doped in the core-shell structure hydrogel, which also proves the existence of the core-shell structure. The design of the core-shell structure enhanced the stability performance of the shell temperature -sensitive hydrogel so that the retention rate of the sample was still 37% at 800 degrees C, and the water retention rate was still 80.7% after repeated immersion in distilled water 7 times, which has good prospects for agricultural and pharmaceutical applications.