Abstract:NiCoCrAlTaY coating is widely used in high temperature oxidation resistance, gas erosion protection and gas path sealing of hot-end parts of aeroengines and gas turbines. In this study, NiCoCrAlTaY coatings were prepared on cobalt-based superalloy substrates by high pressure cold spray technology. The microstructure, mechanical property and tribological behaviors of the coatings before and after thermal exposure at 1050 °C were systemically studied. The results showed that NiCoCrAlTaY coatings with very dense structure could be obtained by high-pressure cold spraying with nitrogen as carrier gas. The coating remained completely intimate with the substrate without any cracking and spalling after thermal exposure at 1050 °C for 500 h. Due to elemental diffusion at high temperatures, the coating formed a four-layer structure, including alumina film on the surface, β-NiAl phase depletion layer near the surface, intermediate layer containing β-NiAl phase and β-NiAl phase depletion layer near the substrate. With the prolongation of thermal exposure at 1050 °C, the thicknesses of β-NiAl phase depletion layers both near the surface and the substrate increased. The thickness and content of the intermediate β-NiAl phase layer decreased gradually during thermal exposure. Besides, the average hardness values of the coating rapidly decreased by about 30 % after thermal exposure at 1050 °C for 5 h. In particular, the hardness of the β-NiAl phase depletion layer near the surface substrate was lower than that of the intermediate area containing β-NiAl phase. Due to the microstructure and hardness evolution, the wear resistance of the coating decreased significantly after thermal exposure. The friction coefficient of the coating increased from 0.2 to 0.5, and the volume wear rate of the thermally exposed coating was about 4.5 times higher than that of the as-sprayed coating. The results of this study provide guidance for design and application of high-performance MCrAlY coatings.

Acoustic Emission Monitoring of the Tensile Behavior of a HVOF-sprayed NiCoCrAlYCe Coating

Microstructure characterization of AlCoCrFeNiTi high-entropy alloy coating produced by atmospheric plasma spraying

Abrasive wear behavior of nano-ceria modified NiCoCrAlY coatings deposited by the high-velocity oxy-fuel process

Numerical and Experimental Investigation for Application of CoNiCrAlY Coatings by HVAF

Cavitation Erosion and Sliding Wear of MCrAlY and NiCrMo Coatings Deposited by HVOF Thermal Spraying

Plasma Spraying NiCoCrAlY-Cr2O3-AgMo Coatings: Fabrication and Tribological Mechanisms

Mechanical property and failure mechanism of coated Al2O3f/SiO2 composites by acoustic emission technology (AE)

Microstructure and mechanical property of high velocity oxy-fuel sprayed WC-Cr3C2-Ni coatings

An Assessment of Coating Thickness on the Microstructure and Mechanical Behavior of IN625 Coating on Ni-Based Superalloy Substrate Deposited by High Velocity Air Fuel Technique

Microstructure and high temperature properties of laser cladded WTaNbMo refractory high entropy alloy coating assisted with ultrasound vibration

Nano- and micro-mechanical properties and corrosion performance of a HVOF sprayed AlCoCrFeNi high-entropy alloy coating

An HVOF-Sprayed (Cr3C2-NiCr+Co) Composite Coating on Ductile Cast Iron: Microstructure, Mechanical Properties, and Scratch Resistance

On the Study of Thermal-Sprayed Ni0.2Co0.6Fe0.2CrSi0.2AlTi0.2 HEA Overlay Coating

Effect of Microstructure and Hardness on Cavitation Erosion and Dry Sliding Wear of HVOF Deposited CoNiCrAlY, NiCoCrAlY and NiCrMoNbTa Coatings

Mechanical property and cracking mechanism of Cr-coated Zr alloy under tensile and compressive loading

MICROSTRUCTURE CHARACTERISTICS OF Cr3C2-NiCr COATINGS DEPOSITED WITH THE HIGH-VELOCITY OXY-FUEL THERMAL-SPRAY TECHNIQUE

Pt-modification on the thermal cycling behavior of NiCoCrAlYTa coating: a case study

Effect of high temperature exposure on microstructure, mechanical and tribological properties of cold sprayed NiCoCrAlTaY coatings

Influence of vacuum annealing temperature on damping performance of NiCrAlY composite coatings

Structural modifications induced by ultrasonic vibration during plasma spray deposition Ni coating on Al substrate

Research on microstructure, mechanical property and wear mechanism of AlCoCrFeNi/WC composite coating fabricated by HVOF