Toughness of Micro-Nano Structure of TaC Dense Ceramic Prepared Using in Situ Technology
Nana Zhao,Yurong Zhao,Xin Wang,Kai Tang,Yunhua Xu,Yiqi Wei,Fuxue Yan,Wenke Meng,Lei Wu,Yuan Fei
DOI: https://doi.org/10.1088/2053-1591/aacd55
IF: 2.025
2018-01-01
Materials Research Express
Abstract:Micro-nano structure of TaC dense ceramic material was prepared using a process of casting and heat treatment. The phase-composition, micro-morphology, crystal structure, and elemental distribution of the TaC dense ceramic were confirmed and analyzed using XRD, SEM, TEM, and EDS. Also, the hardness, elastic modulus, and facture toughness of the material were studied via nano-indentation and micro-indentation. The critical loads of the TaC dense ceramic were then discussed in terms of the two kinds of indentation methods. The results indicate that the hardness and elastic modulus of the TaC dense ceramic material are 28.51 GPa and 556.89 GPa, respectively. The critical load of the material cracking is between 400 mN and 450 mN, and the fracture toughness is 2.23 MPa.m(1/2) according to the nano-indentation method. The critical load of the material cracking is between 500 mN and 1000 mN, and the fracture toughness is 2.94 MPa.m(1/2) according to the micro-indentation method. The R-curve for the micro-nano structure of the TaC dense ceramic material is approximately a straight line, and the fracture toughness is a constant value about the nature of the material. There is crack deflection, grain bridging behavior, and a grain pull-out tendency in the crack propagation of the micro-nano structure of the TaC dense ceramic, and these prove that the fracture toughness of the micro-nano TaC dense ceramic is superior to that of the ordinary ceramic material.