Abstract:Residual stress is the main factor affecting the processing performance and service life of brazed diamond tools. Due to the high melting point of Ni-Cr filler alloy, the difference in thermal expansion coefficient between diamond and brazing layer is large during high brazing temperature, and excessive residual stress tends to be generated at the brazed joint. The existing process parameters are difficult to meet the demand for the lower residual stress under high brazing temperature. Suppressing effectively excessive residual stress has become the focus of current researches for process optimization of brazed diamond. In this paper, the conventional spherical finite element model of diamond is replaced by a six-octahedral finite element model of diamond, and a 3D finite element model of brazed diamond is established. The effects of brazing temperature, brazing layer thickness and holding time on the residual stresses in brazed diamond are analyzed. The results show that higher brazing temperatures result in larger differences in thermal expansion coefficients between the diamond and brazing layer, resulting in larger residual stress. The higher brazing layer thickness will enlarge the stress affected area inside diamond and thus generate higher stress. The residual stress decreases with rising holding time, however, the subsequent thermal damage to the diamond increases. Experimental measured tendency of residual stress for brazed diamond through Raman spectroscopy is well consistent with that of calculated results. After observing of the surface morphology for brazed diamond through super-depth of field microscope, the brazed diamond presents the low residual stress, weak graphitization and excellent processing performance at the condition of brazing temperature of 1010 °C, brazing layer thickness of 0.3 mm and holding time of 5 min.

Microstructure and Performance of Brazed Diamonds with Ni–Cr+multilayer Graphene Composite Alloy

Microstructure and performance of brazed diamonds with multilayer graphene-modified Cu–Sn–Ti solder alloys

Effect of multilayer graphene addition on performance of brazed diamond drill bits with Ni–Cr alloy and its mechanism

Brazing of Large Synthetic Diamond Grits Using Graphene Nanoplatelets Reinforced NiCr Composite Fillers

Effect of Cu Ce Alloy Addition on the Microstructure and Mechanical Performance of Brazed Diamonds with Ni Cr Alloy

Microstructure and Performance of Brazed Diamond Segments with NiCr–x(CuCe) Composite Alloys

Microstructure and properties of brazed diamond with Pr-modified Ni Cr filler metals

Interfacial Microstructure and Mechanical Properties of Brazing Carbon/Carbon Composites to Stainless Steel Using Diamond Particles Reinforced Ag-Cu-Ti Brazing Alloy

Effect of Nd element on the microstructure and mechanical performance of brazed diamonds with Ni–Cr filler metal

Microstructure and Processing Performance of Brazed Diamond Drill Bits with Ni–Cr + Cu–Ce Composite Solder

Microstructure and properties at bonds of diamond grains and Ni Cr filler alloy by fiber laser brazing

Microstructure and Mechanical Properties of Pre-Brazed Diamond Abrasive Grains Using Cu–Sn–Ti Alloy

Interfacial characteristics and thermal damage of brazed W-coated diamond with Ni- based filler alloy

Exploring the trace rare earth Sm on the microstructure and mechanical performance of brazed diamonds by Ni–Cr filler alloy

Cu-induced enhancement of interfacial bonding for brazed diamond grits with NiCr filler alloys

Comparative study on induction brazing of diamond with rare earth Nd-doped crystalline and amorphous Ni-based filler alloy

Effects of Ce and La elements on interfacial bonding, thermal damage and mechanical performance of brazed diamonds with Ni Cr filler alloy

Effect of CeSi2 addition on microstructures of brazed layers and interfacial characteristics of brazed diamonds with NiCr filler alloy

Interfacial microstructure and performance of nano-diamond film/Ti-6Al-4V joint brazed with AgCuTi alloy

Finite element analysis and experimental verification of residual stress in brazed diamond with Ni-Cr filler alloy

Exploring avoiding brittle compounds in brazed joints of C/C composites and DD3 alloys through surface modification