Abstract:To predict brittle fracture in high-strength steels, this study introduces a methodology for analyzing hydrogen-assisted degradation. The proposed approach considers the fully coupled problems of deformation-hydrogen diffusion and cohesive zone modeling. The analysis of hydrogen diffusion assumes that trapped and lattice hydrogen remain in a equilibrium state while accounting for the relationships between the increase in trap sites and plastic strain. The diffusion model simulates hydrogen diffusion in the small scale yielding (SSY) configuration at a crack tip. The simulation results reveal that hydrogen diffusion follows the hydrostatic stress distribution around the crack tip region. Additionally, the plastic strain near this area leads to an increased number of trap sites. Notably, the simulations indicate that lattice hydrogen is the dominant source of embrittlement when a sufficient amount of hydrogen atoms dissolve into the steel, as compared to trapped hydrogen. The hydrogen-assisted degradation evolution is studied by investigating the influence of hydrogen in a cohesive zone modeling (CZM) with a trapezoidal traction separation law (TSL), based on Hydrogen-Enhanced DEcohesion (HEDE) framework. The fully computational framework is utilized to simulate the hydrogen-charged fracture toughness test in a (CT) specimen made of 30CrMo high strength steel. It is demonstrated that the load bearing capacity of the specimen decreases with an increase in the initial hydrogen concentration. Furthermore, the study examines the evolution of the initial crack time with varying initial hydrogen concentrations. The initial hydrogen concentrations are estimated to match the maximum loads observed in the experimental load-displacement curves based on computational framework. The computational CTOD-R curves for hydrogen generally follow the experimental data, the marginally elevated computational CTOD values to underestimate the embrittling in hydrogen-contaminated steel. Overall, the present study proves the capability of this numerical technique to reproduce experimental findings related to hydrogen-assisted fracture.

A Phase-Field Regularized Cohesive Zone Model for Hydrogen Assisted Cracking

A Phase-Field Regularized Cohesion Model for Hydrogen-Assisted Cracking

A phase field formulation for hydrogen assisted cracking

Applications of phase field fracture in modelling hydrogen assisted failures

Numerical Simulation for Hydrogen-Assisted Cracking: An Explicit Phase-Field Formulation

A Phase-Field Framework for Modeling Multiple Cohesive Fracture Behaviors in Laminated Composite Materials

Phase-field simulation of dual-crack system hydrogen embrittlement in metallic materials

A phase field model for elastic-gradient-plastic solids undergoing hydrogen embrittlement

A phase-field regularized cohesive zone model for quasi-brittle materials with spatially varying fracture properties

Computational modelling of hydrogen assisted fracture in polycrystalline materials

Towards Fully Automatic Modelling of the Fracture Process in Quasi-Brittle and Ductile Materials: a Unified Crack Growth Criterion

A phase field model for hydrogen-assisted fatigue

A mechanism-based multi-trap phase field model for hydrogen assisted fracture

Coupling of a Phase-Field Method with a Nonlocal Micro-Mechanical Damage Model for Simulating Ductile Fracture

A Homogenization-Based Phase Field Approach to Fracture with Explicit Dependence on Local Crack Orientation

Numerical analysis of the fully-coupled continuum cohesive modeling on the hydrogen-assisted degradation behavior in high-strength steel

Unified analysis of phase-field models for cohesive fracture

A novel phase‐field based cohesive zone model for modeling interfacial failure in composites

Phase-field cohesive zone modeling of multi-physical fracture in solids and the open-source implementation in Comsol Multiphysics

Phase-Field Modeling of Crack Branching and Deflection in Heterogeneous Media

Hydrogen assisted cracking using an efficient virtual element scheme